Polytron® P30N01
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | Polytron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MzhDLV_Polytron-P30N01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A CHEMICALLY COUPLED 30% LONG FIBER GLASS REINFORCED NATURAL POLYPROPYLENE HEAT STABILIZED FOR INJECTION MOULDING APPLICATION. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.17 | % | ASTM D955 |
| -- | 0.17 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7750 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength | |||
| Yield | 140 | MPa | ASTM D638 |
| Yield | 110 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 2.6 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 6450 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 160 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 18 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 60 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 180 | J/m | ASTM D256 |
| 23°C | 18 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 149 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 167 | °C | ISO 11357-3, ASTM D3418 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature | 750 | °C | IEC 60695-2-13 |
| Flammability | 30 | mm/min | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 101CC SI | RTP Company | PP Homopolymer | RTP |
| VENYL UE030 | AD majoris | Nylon 66 | VENYL |
| TUFNYL® RXXIC BLACK | SRF Ltd. | Nylon 66 | TUFNYL® |
| YUNGSOX® PP 5003 | Formosa Polypropylene | PP Random Copolymer | YUNGSOX® PP |
| Felix Compounds Mica | Felix Compounds | PP+PE | Felix Compounds |