EMOPLEN® CP GFR 20 FR V0
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | EMAS Plastik San.Tic.AS. |
| Trademark: | EMOPLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MyqzIe_EMOPLEN-CP-GFR-20-FR-V0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene copolymer %20 glass fiber reinforced, V0 flamm. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 - 1.30 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 - 18 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.35 - 0.55 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 65 - 70 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4000 - 7500 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 50.0 - 80.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 4.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | > 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 110 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 110 | °C | ISO 306/B |
| Melting Temperature (DSC) | 160 | °C | ISO 3146 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 | |
| Glow Wire Ignition Temperature | 960 | °C | VDE 0471/2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP PP 20 TALC | RTP Company | PP, Unspecified | RTP |
| ADENE NCZA | A.D. Compound spa | PP Homopolymer | ADENE |
| APEX® 3703-55NT1 | Teknor Apex Company | PVC, Flexible | APEX® |
| Grilamid® L 16 nat | EMS-GRIVORY | Nylon 12 | Grilamid® |
| LEXAN™ 503R resin | SABIC Innovative Plastics | PC | LEXAN™ |