EVAL™ SP295
| Category: | EVOH , Ethylene Vinyl Alcohol |
| Manufacturer: | Kuraray Co., Ltd. |
| Trademark: | EVAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MyepAf_EVAL-SP295.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Orientability Ethylene Vinyl Alcohol Copolymer Applications: Shrink Film, Skin Packaging and thermoforming |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 5.4 | g/10 min | ISO 1133 |
| 210°C/2.16 kg | 12 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 25.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 12 | % | ISO 527-2 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability | ISO 14663-2 | ||
| 20°C, 65% RH | 0.035 | cm³·mm/m²/atm/24 hr | ISO 14663-2 |
| 20°C, 85% RH | 0.085 | cm³·mm/m²/atm/24 hr | ISO 14663-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 47.0 | °C | ISO 11357-2 |
| Melting Temperature | 163 | °C | ISO 11357 |
| Peak Crystallization Temperature | 145 | °C | ISO 11357-3 |
| Additional Information |
|---|
| Limit of Orientability, Simultaneous, Kuraray Method: 4.5 x 4.5 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx 663E0 | The Matrixx Group, Inc. | Nylon 66 | Matrixx |
| Razamid® A121U GR20-50 | Razin™ Engineering Plastics | Nylon 66 | Razamid® |
| TABOREN PH 81 G 30 | SILON s.ro | PP Homopolymer | TABOREN |
| Fainplast PVC RK 112 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| ESTOPLAST EP 4140GY01 | Ester Industries Ltd. | PBT | ESTOPLAST EP |