| Staramide PF004EUC is a 20 % Glass Fiber Reinforced Polyamide 6 Injection Molding Resin |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (4.00 mm) | 0.34 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6300 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 117 | MPa | |
| Break | 110 | MPa | |
| Tensile Strain (Yield) | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 4800 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| -- 3 | 163 | MPa | |
| -- 4 | 147 | MPa | |
| Flexural Strain at Break 5 | 7.6 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 6(23°C) | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 7(23°C) | 40 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 8(1.8 MPa, Unannealed, 64.0 mm Span) | 177 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (1.60 mm) | 650 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 240 to 270 | °C | |
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Yield |
| 4 . | Break |
| 5 . | 2.0 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAN AE8200 | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| Nanjing Hongrui PC CS1000 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PC | Nanjing Hongrui PC |
| Axiall PVC 1702 Clear 7070 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| ColorRx® PC2-1500RX | LTL Color Compounders, Inc. | PC | ColorRx® |
| ExxonMobil™ HDPE HD 6605.70 | ExxonMobil Chemical | HDPE Copolymer | ExxonMobil™ HDPE |