Hanwha Total PE 531G
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Trademark: | Hanwha Total PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MwQHx9_Hanwha-Total-PE-531G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 531G is a low-density polyethylene resin for protestive films. This grade is designed to be processed in conventional blown film equipment. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.8 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 12.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 700 | % | ASTM D638 |
| Coefficient of Friction | 0.25 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 40 µm | 22.6 | MPa | ASTM D882 |
| TD : Break, 40 µm | 15.7 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 40 µm | 240 | % | ASTM D882 |
| TD : Break, 40 µm | 590 | % | ASTM D882 |
| Dart Drop Impact (40 µm) | 65 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 1 |
| Melting Temperature | 113 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (40.0 µm) | 6.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Blocking, SAMSUNG TOTAL: 650 g/10cm³ |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 150 - 160 | °C | |
| Cylinder Zone 2 Temp. | 150 - 160 | °C | |
| Cylinder Zone 3 Temp. | 150 - 160 | °C | |
| Cylinder Zone 4 Temp. | 150 - 160 | °C | |
| Cylinder Zone 5 Temp. | 150 - 160 | °C | |
| Die Temperature | 160 | °C |
| Extrusion instructions |
|---|
| Blow up ratio: 1 to 2 |
| Note Message | |
|---|---|
| 1 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 600 TFE 10 HB | RTP Company | ABS | RTP |
| Qenos PE GM5049B | Qenos Pty Ltd | HDPE, HMW | Qenos PE |
| Ferro PP TPP40AF57UL WHITE | Ferro Corporation | PP Homopolymer | Ferro PP |
| 3M™ Dyneon™ Perfluoroelastomer PFE E-21464 | 3M Advanced Materials Division | Perfluoroelastomer | 3M™ Dyneon™ Perfluoroelastomer |
| Sylvin 9812-82 Grey 9611 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |