Riblene® FL 23 I
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Riblene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MvKddk_RibleneFL23I.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Riblene FL 23 I is a low density polyethylene (LDPE) additivated with slip agent, ideal for blown film extrusion. Riblene FL 23 I is characterised by a good balance between proc-essability and mechanical properties. Films manufactured with Riblene FL 23 I are easily heat shrinkable and characterised by good optical and mechanical properties. Main Applications Riblene FL 23 I is recommended for general blown film applications, for the production of low gauge film and shrink film, for lamination and for blending. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.2 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | 0.13 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Film Thickness - Recommended / Available | 25 to 80 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% secant, MD : 40 µm, blown film | 180 | MPa | ISO 527-3 |
| 1% secant, TD : 40 µm, blown film | 190 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 40 µm, blown film | 11.0 | MPa | ISO 527-3 |
| TD : Yield, 40 µm, blown film | 11.0 | MPa | ISO 527-3 |
| MD : Broken, 40 µm, blown film | 25.0 | MPa | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 22.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 40 µm, blown film | 300 | % | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 650 | % | ISO 527-3 |
| Dart Drop Impact 1(40 µm, Blown Film) | 130 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 40.0 µm | 80.0 | kN/m | ISO 6383-2 |
| TD : 40.0 µm | 55.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 93.0 | °C | ISO 306/A |
| Melting Temperature | 113 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 40.0 µm, Blown Film) | 72 | ASTM D2457 | |
| Haze (40.0 µm, Blown Film) | 5.5 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 190 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miramid® SE25C | BASF Leuna GmbH | Nylon 66 | Miramid® |
| Shin-Etsu Elastomer FE-381U | Shin-Etsu Silicones of America | Fluoro Si | Shin-Etsu Elastomer |
| apilon 52® D 25L | API SpA | TPU-Polyester | apilon 52® |
| Karina IVORY PVC COMPOUND 70911-35/ 1-HY-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Braskem PP DR155.01 | Braskem Europe GmbH | PP Random Copolymer | Braskem PP |