Order Products : sales@su-jiao.com

Sasol Polymers PE HF123

Category:	LLDPE , Linear Low Density Polyethylene
Manufacturer:	Sasol Polymers
Trademark:	Sasol Polymers PE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Mv6Qoy_Sasol-Polymers-PE-HF123.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Features

Hexene copolymer

Outstanding mechanical properties

Excellent drawdown

Good heat sealing range

Good stiffness

Applications

General packaging thin film (10µm to 30µm)

Not recommended for lamination film

Blending into LDPE

General Information
Additive	High smoothness High caking resistance Antioxidation
Features	Rigid, good High smoothness High caking resistance Copolymer hexene comonomer Antioxidation Good stripping Good heat sealability Compliance of Food Exposure
Uses	Packaging Films Mixing
Agency Ratings	EC 1935/2004 FDA 21 CFR 177.1520(a)(3)(i)(c)(1) FDA 21 CFR 177.1520(c) 3.1a
Forms	Particle
Processing Method	Blow film

Physical	Nominal Value	Unit	Test Method
Density	0.929	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.0	g/10 min	ASTM D1238

Mechanical	Nominal Value	Unit	Test Method
Coefficient of Friction			ASTM D1894
With itself-dynamic, blown film	0.12		ASTM D1894
With itself-static, blown film	0.12		ASTM D1894

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	30	µm
Tensile Strength			ASTM D882
MD : Yield, 30 µm, blown film	12.0	MPa	ASTM D882
TD : Yield, 30 µm, blown film	12.0	MPa	ASTM D882
MD : Broken, 30 µm, blown film	33.0	MPa	ASTM D882
TD : Broken, 30 µm, blown film	23.0	MPa	ASTM D882
Tensile Elongation			ASTM D882
MD : Yield, 30 µm, blown film	500	%	ASTM D882
TD : Yield, 30 µm, blown film	580	%	ASTM D882
Dart Drop Impact ¹(30 µm, Blown Film)	150	g	ASTM D1709
Elmendorf Tear Strength			ASTM D1922
MD : 30 µm, blown film	8.0	g	ASTM D1922
TD : 30 µm, blown film	27	g	ASTM D1922

Optical	Nominal Value	Unit	Test Method
Gloss (45°)	45		ASTM D2457
Haze	15	%	ASTM D1003

Additional Information
The above values were calculated from data for 30µm film produced on a 75mm Barmag extruder with 190°C melt temperature using a 2:1 blow ratio.

Extrusion	Nominal Value	Unit
Hopper Temperature	180 - 190	°C
Cylinder Zone 1 Temp.	190 - 200	°C
Cylinder Zone 2 Temp.	190 - 200	°C
Cylinder Zone 3 Temp.	190 - 200	°C
Cylinder Zone 4 Temp.	190 - 200	°C
Melt Temperature	190	°C
Die Temperature	190 - 200	°C

Extrusion instructions
Screen Pack: 20/40/20 BS meshBlow ratio: >2:1

Note Message
1 .	F50

Resin Grade	Manufacturer	Category	Trademark
MAXAMID™ EPDM66G14-BK09	Pier One Polymers, Inc.	Nylon 66	MAXAMID™
DENITER C 3010	Vamp Tech	PC+PBT	DENITER
Gallonprene® GP100-4001	Shenzhen Sungallon Rubber & Plastic Corporation Limited	TPE	Gallonprene®
LEXAN™ HFD4413 resin	SABIC Innovative Plastics Asia Pacific	PC	LEXAN™
LG ASA LI913	LG Chem Ltd.	ASA	LG ASA