4MID® 9B22150 GF50
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | 4Plas |
| Trademark: | 4MID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MtWmD4_4MID-9B22150-GF50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4MID 9B22150 is a Near Prime Standard Flow 50% Glass Fibre Reinforced PA6 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.55 | g/cm³ | ISO 1183 |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 1.5 | % | ISO 62 |
| Moisture Content | < 2000 | ppm | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 13500 | MPa | ISO 527-2/5 |
| Tensile Stress (Break, 23°C) | 160 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus 2(23°C) | 10500 | MPa | ISO 178 |
| Flexural Stress 3(23°C) | 300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 65 | kJ/m² | ISO 179/1eU |
| 23°C | 75 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 10 | kJ/m² | ISO 180/1A |
| 23°C | 14 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 215 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 210 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 210 | °C | ISO 306/B |
| Melting Temperature 4 | 223 | °C | ISO 11357 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 650 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 60.0 - 100 | °C | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 - 100 | MPa | |
| Screw Speed | 200 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 60 - 80 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 24 Hrs |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3412 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Chemical Resources LD10919 | Chemical Resources, Inc. | LDPE | Chemical Resources |
| KOPLA PET KEG1030 | KOPLA Co., Ltd. | PET | KOPLA PET |
| Geon™ Vinyl Rigid Extrusion 06935L | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| ULTEM™ CRS5201R resin | SABIC Innovative Plastics | PEI | ULTEM™ |