Order Products : sales@su-jiao.com
LNP™ COLORCOMP™ FR15C compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ COLORCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MsKYGe_LNPCOLORCOMPFR15Ccompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
COLORCOMP* FR15C is a compound based on ABS (non-PBBE additive) containing Flame Retardant. Added features include: Good Property/Toughness, Excellent Moldability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.20 | g/cm³ | ASTM D792 |
| -- | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/3.8 kg | 4.0 | g/10 min | ASTM D1238 |
| 220°C/5.0 kg | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2340 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield 2 | 41.4 | MPa | ASTM D638 |
| Yield | 41.3 | MPa | ISO 527-2/50 |
| Fracture 3 | 35.2 | MPa | ASTM D638 |
| Fracture | 31.3 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 2.3 | % | ASTM D638 |
| Yield | 2.1 | % | ISO 527-2/50 |
| Fracture 5 | 9.0 | % | ASTM D638 |
| Fracture | 34 | % | ISO 527-2/50 |
| Flexural Modulus 6(50.0 mm Span) | 2720 | MPa | ASTM D790 |
| Flexural Strength 7(Yield, 50.0 mm Span) | 71.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 8(23°C) | 20 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 210 | J/m | ASTM D256 |
| -30°C 9 | 6.5 | kJ/m² | ISO 180/1A |
| 23°C 10 | 19 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 33.9 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 82.2 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 70.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 11 | 73.4 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 86.1 | °C | ASTM D1525 12 |
| -- | 81.2 | °C | ISO 306/B50 |
| -- | 84.1 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 8.5E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 8.6E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance 13 | PLC 7 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 4 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm | V-0 | UL 94 | |
| 2.5 mm | 5VA | UL 94 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (200°C, 1000 sec^-1) | 290 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82 - 88 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Drying Time, Maximum | 6.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Suggested Shot Size | 50 - 70 | % | |
| Rear Temperature | 171 - 182 | °C | |
| Middle Temperature | 193 - 204 | °C | |
| Front Temperature | 199 - 216 | °C | |
| Nozzle Temperature | 199 - 221 | °C | |
| Processing (Melt) Temp | 199 - 221 | °C | |
| Mold Temperature | 49 - 71 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 30 - 60 | rpm | |
| Vent Depth | 0.038 - 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 sp=62mm |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 标准 B (120°C/h), 载荷2 (50N) |
| 13 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 6555 | Covestro - Polycarbonates | PC | Makrolon® |
| SAXAMID™ 126F5 | SAX Polymers | Nylon 6 | SAXAMID™ |
| NYLOY® MG-1020NM-1 | Nytex Composites Co., Ltd. | Nylon 66 | NYLOY® |
| LEXAN™ LUX2489D resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| Sylvin 4200-85 Grey 9572 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |