Ultramid® HPN 9350 HS
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MsGphB_Ultramid-HPN-9350-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid HPN 9350 HS is a flexible, heat stabilized, impact modified PA6 extrusion grade resin. It possesses a balance of performance properties such as good flexibility, toughness and abrasion resistance. The addition of heat stabilizer system extends its retention of properties at elevated temperatures. Chemical resistance is excellent to greases, oils, and hydrocarbons. Applications Ultramid HPN 9350 HS is generally recommended for applications such as automotive under hood tubing, windshield washer tubing, cable jacketing, and other tubing. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.06 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 1.3 | -- | % | |
| Water Absorption | ||||
| Saturation | 6.8 | -- | % | ASTM D570 |
| Saturated, 23°C | 6.8 | -- | % | ISO 62 |
| Balance, 50% RH | 1.9 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.9 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 80 | -- | ASTM D785 | |
| Ball Indentation Hardness | 70.0 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 1700 | -- | MPa | ISO 527-2 |
| Tensile Strength | ||||
| Yield, 23°C | 50.0 | -- | MPa | ASTM D638 |
| Yield, 23°C | 45.0 | -- | MPa | ISO 527-2 |
| Tensile Elongation | ||||
| Yield, 23°C | 5.0 | -- | % | ASTM D638 |
| Yield, 23°C | 4.5 | -- | % | ISO 527-2 |
| Fracture, 23°C | > 100 | -- | % | ASTM D638 |
| Nominal Tensile Strain at Break (23°C) | > 50 | -- | % | ISO 527-2 |
| Flexural Modulus | ||||
| -40°C | 2280 | -- | MPa | ASTM D790 |
| 23°C | 1730 | 520 | MPa | ASTM D790 |
| 65°C | 375 | 315 | MPa | ASTM D790 |
| 90°C | 220 | 240 | MPa | ASTM D790 |
| 121°C | 190 | 210 | MPa | ASTM D790 |
| 23°C | 1450 | -- | MPa | ISO 178 |
| Flexural Strength | ||||
| -40°C | 105 | 120 | MPa | ASTM D790 |
| 23°C | 69.0 | 25.0 | MPa | ASTM D790 |
| 65°C | 15.0 | 15.0 | MPa | ASTM D790 |
| 90°C | 10.0 | 10.0 | MPa | ASTM D790 |
| 121°C | 9.50 | 10.0 | MPa | ASTM D790 |
| 23°C | 50.0 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 9.0 | -- | kJ/m² | ISO 179 |
| 23°C | 40 | -- | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | -- | ISO 179 | |
| Notched Izod Impact (23°C) | 590 | -- | J/m | ASTM D256 |
| Drop Impact Resistance (23°C) | 190 | -- | J | Internal method |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Flange temperature | 225 - 240 | °C | |
| Head Temperature | 225 - 245 | °C | |
| Extruder Screw L/D Ratio | 20.0:1.0 to 24.0:1.0 | ||
| Extruder Screw Compression Ratio | 3.5:1.0 to 4.0:1.0 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 1.8 MPa, not annealed | 55.0 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 50.0 | -- | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418, ISO 3146 |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Cylinder Zone 1 Temp. | 245 - 260 | °C | |
| Cylinder Zone 3 Temp. | 240 - 255 | °C | |
| Cylinder Zone 5 Temp. | 240 - 250 | °C | |
| Melt Temperature | 240 - 250 | °C | |
| Die Temperature | 225 - 240 | °C |
| Extrusion instructions |
|---|
| Screw Parameters Metering Section : 40% Transition Section : 6 to 7 flights Feed Section : balance of screw length |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ULTEM™ 2310R resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| Elexar® EL-1934G | Teknor Apex Company | TPE | Elexar® |
| Karina BLACK PVC COMPOUND 722-48/ 1-A-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 65-8498 | Lehmann & Voss & Co. | PP Copolymer | LUVOCOM® |
| Vipel® F737-BCX-00 | AOC, L.L.C. | Polyester Alloy | Vipel® |