Order Products : sales@su-jiao.com
SABIC® HDPE CC253SL
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Mrxdwp_SABIC-HDPE-CC253SL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE CC253SL offers a good combination of stiffness, impact resistance, ESCR and organoleptic properties. The typical applications of this grade are mainly injection moulding and compression moulding of caps for sparkling water and carbonated soft drinks. SABIC® HDPE CC253SL does contain slip agent for an easier opening. It is stabilised against UV light because the slip agent is sensitive to light; exposure to sunlight should be avoided. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.952 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.8 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 1100 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00 mm, Compression Molded | 26.0 | MPa | |
| Break, 2.00 mm, Compression Molded | 30.0 | MPa | |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | > 200 | % | ISO 527-2/1BA/50 |
| Flexural Modulus (2.00 mm, Compression Molded) | 1150 | MPa | ISO 178 |
| Flexural Stress (2.00 mm, Compression Molded) | 26.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C, Compression Molded) | 7.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 80.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 124 | °C | ISO 306/A |
| Melting Temperature (DSC) | 131 | °C | ISO 11357-3 |
| Enthalpy Change | 201 | J/g | ISO 11357-3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene MBW3291 | Teknor Apex Asia Pacific PTE. LTD. | LLDPE | Sinpolene |
| Nypol® PA B3 G10 V20 CNZ0029 NT398 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| Amilan® CM1023G1000 | Toray Resin Company | Nylon 6 | Amilan® |
| INSTRUC PESGF30 | Infinity LTL Engineered Compounds | PESU | INSTRUC |
| LNP™ LUBRICOMP™ RCL36S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |