Starex LH-0300
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MqYYWx_Starex-LH-0300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex LH-0300 is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 10 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955, ISO 2577 | ||
| Flow : 3.20 mm | 0.42 | % | |
| Across Flow : 3.20 mm | 0.48 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1700 | MPa | ASTM D638 |
| -- | 1890 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 35.0 | MPa | ASTM D638 |
| Yield | 36.0 | MPa | ISO 527-2/50 |
| Break 3 | 32.0 | MPa | ASTM D638 |
| Break | 34.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 51 | % | ASTM D638 |
| Break | 60 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 1700 | MPa | ASTM D790 |
| -- 6 | 2060 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 46.0 | MPa | ASTM D790 |
| -- 8 | 58.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 16 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 150 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 98 | J/m | ASTM D256 |
| 23°C 10 | 17 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 99.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 94.0 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 103 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 88.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 80.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 4.00 mm | 100 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 100 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 120 | °C | |
| Desiccant Dryer | 120 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 280 to 290 | °C | |
| Middle Temperature | 300 to 310 | °C | |
| Front Temperature | 320 to 330 | °C | |
| Nozzle Temperature | 330 | °C | |
| Mold Temperature | 100 to 140 | °C | |
| Injection Pressure | 108 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsamid® AMVO TLD | Arkema | Nylon 12 | Rilsamid® |
| Syncure™ System S100FH | PolyOne Corporation | XLPE | Syncure™ |
| Niretan B F10 | Soredi S.p.a. | Nylon 6 | Niretan B |
| GLS PP YT06 (PP30 Talc) | GLS Polymers Pvt. Ltd. | PP, Unspecified | GLS PP |
| GPPS Microgranulates 130M | INEOS Styrenics International SA | PS (GPPS) | GPPS Microgranulates |