CV77518 resin is a polyethylene plastomer designed for blown and cast film extrusion that contains no slip and no antiblock additives. Films produced with this resin exhibit a very low seal initiation temperature with a broad hot tack window. Other features of this resin include higher stiffness, high melting point, and ease of processing for narrow die gaps. Application/Uses: Blown film Cast film Packaging |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ASTM D4883 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus 1 | ASTM D882 | ||
| 1% secant, MD : 25 µm, blown film | 152 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film | 172 | MPa | ASTM D882 |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 35.0 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 40.0 | MPa | ASTM D882 |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 700 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 1200 | % | ASTM D882 |
| Dart Drop Impact 4(25 µm, Blown Film) | 400 | g | ASTM D1709A |
| Elmendorf Tear Strength 5 | ASTM D1922 | ||
| MD : 25 µm, blown film | 300 | g | ASTM D1922 |
| TD : 25 µm, blown film | 550 | g | ASTM D1922 |
| Seal Initiation Temperature 6(25 µm, Blown Film) | 88.0 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.4 µm, Blown Film) | 55 | ASTM D2457 | |
| Haze (25.4 µm, Blown Film) | 13 | % | ASTM D1003 |
| Additional Information |
|---|
| Extrusion conditions used to produce 1 mil (0.025 mm) film include a 6" die, 2.5" 24:1 L:D barrier screw, 2.4:1 BUR, 100-mil die gap, 15" frostline height, 400° F melt temperature, and 7.5 lb/hr/inch die output. Density results are on Base Resin. |
| Note Message | |
|---|---|
| 1 . | Test run at 23°C (73°F) and 50% relative humidity |
| 2 . | Test run at 23°C (73°F) and 50% relative humidity |
| 3 . | Test run at 23°C (73°F) and 50% relative humidity |
| 4 . | Test run at 23°C (73°F) and 50% relative humidity |
| 5 . | Test run at 23°C (73°F) and 50% relative humidity |
| 6 . | Seal initiation temperature is the temperature at which 200 g/inch seal strength is achieved. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 95610CSU10 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Trademark PP PPH140E | Trademark Plastics Corporation | PP Homopolymer | Trademark PP |
| TYNEA 3100 | Tyne Plastics LLC. | Acetal (POM) Homopolymer | TYNEA |
| Borealis PE FG5190 | Borealis AG | LLDPE | Borealis PE |
| PLUSTEK PB508 | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |