Estane® 5703 TPU
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Estane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MolbzH_Estane-5703-TPU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Type: Estane® 5703 is a Polyester Type Thermoplastic Polyurethane (TPU). Features: Soft Compound with High Elongation, Displays Low Temperature Flexibility and Abrasion Resistance. It can be processed by means of solution coating, extrusion and melt coating. Application:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 70 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| -- | 31.0 | MPa | |
| 100% Strain | 2.30 | MPa | |
| 300% Strain | 3.80 | MPa | |
| Tensile Elongation (Break, 0.762 mm) | 630 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 2.30 | MPa | |
| 300% Strain | 3.80 | MPa | |
| Tensile Strength (Break) | 31.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 630 | % | ASTM D412 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature 1 | -31.0 | °C | DSC |
| Kofler Melting Temperature | 85 | °C | ASTM D1525 |
| Ring and Ball Softening Point | 179 | °C | ASTM E28-92 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brookfield Viscosity 2 | |||
| 15% T.S. in Cyclohexanone : 23°C | 1.60 | Pa·s | |
| 15% T.S. in MEK/Toluene : 23°C | 0.250 | Pa·s |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Adhesion to PET 3 | 305.9 | g/2.5 cm | |
| Gradient Bar Tack Temperature | 91 | °C | |
| Open Time | > 5.0 | min | ASTM D4497-94 |
| T-Peel | ASTM D1876 | ||
| Aluminum Foil | 1.8 | kN/m | |
| Mylar Film | 3.4 | kN/m |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (204°C) | 92.0 | Pa·s | ASTM D1084 |
| Note Message | |
|---|---|
| 1 . | 10°C/min, second heat |
| 2 . | RVT Spindle #2, 20 RPM |
| 3 . | TP-141 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Braskem PE F 7018 | Braskem | LDPE | Braskem PE |
| Ferro PP TPP20AE09HB WHITE | Ferro Corporation | PP Homopolymer | Ferro PP |
| Hifax HKC 426P BLACK | LyondellBasell Industries | PP Homopolymer | Hifax |
| KumhoSunny PC/ABS HAC8250NH-DF30 | Shanghai KumhoSunny Plastics Co., Ltd. | PC+ABS | KumhoSunny PC/ABS |
| Monprene® CP-19234 | Teknor Apex Company | TPE | Monprene® |