Ultramid® 8234G HS BK-102
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Moe39B_Ultramid-8234G-HS-BK-102.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid 8234G HS BK-102 is heat stabilized, pigmented black, 44% glass reinforced PA6 injection molding compound offering the highest level of strength, stiffness, high temperature performance and dimensional stability. Its resistance to creep under load is excellent. It maintains its inherent chemical resistance to greases, oils and hydrocarbons. It is available in natural and black versions. Pigmented and weatherable versions may be offered on a case by case basis. Ultramid 8234G HS BK-102 is generally recommended for applications such as consumer power tool housings, cattle ear taggers, luggage frames, fans and pressure regulator housings. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.49 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | -- | % | |
| Water Absorption | ||||
| 24 hr | 0.90 | -- | % | ASTM D570 |
| 23°C, 24 hr | 0.90 | -- | % | ISO 62 |
| Saturation | 5.2 | -- | % | ASTM D570 |
| Saturation, 23°C | 5.2 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 1.5 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.5 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | ||||
| Break, 23°C | 193 | 145 | MPa | ASTM D638 |
| Break, 23°C | 195 | -- | MPa | ISO 527-2 |
| Tensile Elongation | ||||
| Break, 23°C | 2.0 | 6.0 | % | ASTM D638 |
| Break, 23°C | 2.0 | -- | % | ISO 527-2 |
| Flexural Modulus | ||||
| -40°C | 12300 | 14700 | MPa | ASTM D790 |
| 23°C | 11700 | 6560 | MPa | ASTM D790 |
| 65°C | 7000 | -- | MPa | ASTM D790 |
| 121°C | 4830 | -- | MPa | ASTM D790 |
| 23°C | 11800 | -- | MPa | ISO 178 |
| Flexural Strength | ||||
| -40°C | 450 | 410 | MPa | ASTM D790 |
| 23°C | 352 | 212 | MPa | ASTM D790 |
| 65°C | 220 | -- | MPa | ASTM D790 |
| 90°C | 160 | -- | MPa | ASTM D790 |
| 121°C | 138 | -- | MPa | ASTM D790 |
| 23°C | 290 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | -- | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 70 | -- | kJ/m² | ISO 179 |
| Notched Izod Impact | ||||
| 23°C | 130 | -- | J/m | ASTM D256 |
| 23°C | 14 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 210 | -- | °C | ASTM D648, ISO 75-2/A |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418, ISO 3146 |
| CLTE - Flow | 3.1E-5 | -- | cm/cm/°C | ASTM E831 |
| RTI Elec | UL 746 | |||
| 0.710 mm | 130 | -- | °C | |
| 1.50 mm | 140 | -- | °C | |
| 3.00 mm | 140 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.710 mm | 95.0 | -- | °C | |
| 1.50 mm | 105 | -- | °C | |
| 3.00 mm | 105 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.710 mm | 130 | -- | °C | |
| 1.50 mm | 140 | -- | °C | |
| 3.00 mm | 140 | -- | °C |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Drop Weight Impact Strength (23°C) | 3.25 | -- | J | Internal Method |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.060 | % | |
| Processing (Melt) Temp | 280 to 305 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DIOSHY® MP-865 | DIOSHY Co.,Ltd. | SBS | DIOSHY® |
| Franprene TVA 9155 | Franplast S.r.l. | SEBS | Franprene |
| Karina IVORY PVC COMPOUND -E 832-35/ 1-Y-ERYB-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OTECH PVC OW135 - Wire Jacket | OTECH Corporation | PVC, Unspecified | OTECH PVC |
| LNP™ THERMOCOMP™ WF006 compound | SABIC Innovative Plastics | PBT | LNP™ THERMOCOMP™ |