VENYL UN020
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MnuB0R_VENYL-UN020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL UN020 is an unreinforced polyamide 66 with improved impact resistance intended for Injection moulding. APPLICATIONS VENYL UN020 has been developed especially for very demanding applications in automotive industry and electrical parts. Products requiring excellent combination between rigidity and impact resistance at room temperature. It allows to avoid the conditioning of the part before use (low moisture absorption). VENYL UN020 is available in both natural and black (VENYL UN020 BLACK 8229) but other colours can be provided on request. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.11 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 1.4 - 2.3 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.4 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (L-Scale) | 100 | 85 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3250 | 1500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 70.0 | 53.5 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 15 | 40 | % | ISO 527-2 |
| Flexural Modulus | 2000 | 1030 | MPa | ISO 178 |
| Flexural Stress | 110 | 50.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 14 | 60 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | No Break | No Break | ISO 179 | |
| Notched Izod Impact | -- | No Break | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 205 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 100 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 256 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Oxygen Index | 22 | -- | % | ISO 4589-2 |
| Additional Information |
|---|
| 干燥 Water Absorption 23°C/50%RH, ISO 62: 2.2 to 2.5%Tensile Stress at Break, ISO 527-1,-2: 65 to 75 MPaTensile Modulus, ISO 527-1,-2: 3000 to 3500 MPaFlexural Strength, ISO 178: 100 to 120 MPaFlexural Modulus, ISO 178 1900 to 2100 MPaCharpy Notched Impact Strength, ISO 179: 11 to 17 kJ/m²Izod Notched Impact Strength, ISO 180: 160 to 198 J/m |
| 调节后的 Tensile Stress at Break, ISO 527-1,-2: 50 to 55 MPaTensile Modulus, ISO 527-1,-2: 1400 to 1600 MPaFlexural Strength, ISO 178: 55 to 65 MPaFlexural Modulus, ISO 178 950 to 1100 MPaCharpy Notched Impact Strength, ISO 179: 50 to 70 kJ/m² |
| Injection | Dry | Unit | |
|---|---|---|---|
| Rear Temperature | 260 - 270 | °C | |
| Middle Temperature | 270 - 280 | °C | |
| Front Temperature | 275 - 290 | °C | |
| Processing (Melt) Temp | 265 - 280 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C | |
| Injection Pressure | 60.0 - 100 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 35.0 - 60.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1980 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Sindustris PC GP5201 | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| NEMCON H PP DP172 | Ovation Polymers Inc. | PP, Unspecified | NEMCON H |
| Magnobond 6155 | Magnolia Plastics, Inc. | Epoxy | Magnobond |
| POLYCASA® CAST | Polycasa | Acrylic (PMMA) | POLYCASA® |