Sarlink® TPV X6155N
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPV |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MkQOGX_Sarlink-TPV-X6155N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sarlink® X6155N is an engineered material designed primarily for demanding consumer and automotive interior applications. Available only in natural, Sarlink® X6155N exhibits excellent compression set and flex fatigue, high and low temperature performance. The material can be processed by injection molding and extrusion for applications such as building profiles, interior car applications, colored applications, over molding and translucent products. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.882 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shaw A, 5 seconds, extruded | 53 | ISO 868 | |
| Shore A, 5 seconds, injection molding | 53 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| Transverse flow : 100% strain | 4.90 | MPa | ISO 37 |
| Flow : 100% strain | 1.90 | MPa | ISO 37 |
| Tensile Stress | ISO 37 | ||
| Acos flow : Yield | 3.90 | MPa | ISO 37 |
| Flow : Yield | 4.00 | MPa | ISO 37 |
| Tensile Elongation | ISO 37 | ||
| Transverse flow : Fracture | 700 | % | ISO 37 |
| Flow : Fracture | 450 | % | ISO 37 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 27 | % | ISO 815 |
| 70°C, 22 hr | 33 | % | ISO 815 |
| 100°C, 22 hr | 36 | % | ISO 815 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 - 215 | °C | |
| Middle Temperature | 180 - 215 | °C | |
| Front Temperature | 180 - 215 | °C | |
| Nozzle Temperature | 187 - 220 | °C | |
| Processing (Melt) Temp | 185 - 220 | °C | |
| Mold Temperature | 10.0 - 55.0 | °C | |
| Back Pressure | 0.100 - 1.00 | MPa | |
| Screw Speed | 100 - 200 | rpm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 180 - 200 | °C | |
| Cylinder Zone 2 Temp. | 180 - 205 | °C | |
| Cylinder Zone 3 Temp. | 187 - 210 | °C | |
| Cylinder Zone 4 Temp. | 187 - 210 | °C | |
| Melt Temperature | 195 - 215 | °C | |
| Die Temperature | 195 - 215 | °C | |
| Take-Off Roll | 20.0 - 50.0 | °C |
| Extrusion instructions |
|---|
| Screen Pack: 20 to 60 meshScrew: 3:1 Compression Ratio |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Taitacell EPS 321S | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| Capilene® SE 50 E | Carmel Olefins Ltd. | PP Impact Copolymer | Capilene® |
| Leona™ CR302 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| Pro-fax PL395N | INDELPRO, S.A. de C.V. | PP Homopolymer | Pro-fax |
| Moplen HP600R | PolyMirae | PP Homopolymer | Moplen |