Spartech Polycom SC7F-7010
| Category: | PC , Polycarbonate |
| Manufacturer: | Spartech Polycom |
| Trademark: | Spartech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Miplgc_Spartech-Polycom-SC7F-7010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Spartech SC7F-7010 is a medium viscosity, flame retardant, PC resin for injection molding. It is heat stabilized and lubricated for good processing characteristics. Polycarbonate resins span a wide range of physical properties that combine to make it one of the toughest, most versatile of all engineering thermoplastics. It is well known for its exceptional impact resistance, plus it has outstanding mechanical, electrical, and optical properties. A very versatile product for a wide variety of applications, Spartech SC7F-7010 is recommended for industrial, transportation, sporting goods and electrical/electronic applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 14 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 62.1 | MPa | ASTM D638 |
| Flexural Modulus (23°C) | 2240 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 750 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 132 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm, NC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 271 - 282 | °C | |
| Front Temperature | 282 - 299 | °C | |
| Nozzle Temperature | 277 - 304 | °C | |
| Processing (Melt) Temp | 288 - 316 | °C | |
| Mold Temperature | 71.1 - 93.3 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toyolac® AX05-X38 | Toray Resin Company | ABS | Toyolac® |
| TPSiV™ 3345-65A NAT 25564 | Multibase, A Dow Corning Company | TPSiV | TPSiV™ |
| WPP PP PPHFGC-3 | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| CP PRYME® Nylon 66 NN100STL NAT | Chase Plastics Services Inc. | Nylon 66 | CP PRYME® Nylon 66 |
| Polifor® C 30 TE/40 BIANCO 0330 | SO.F.TER. SPA | PP Copolymer | Polifor® |