Adflex KS084P
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Adflex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Mi70kI_Adflex-KS084P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Adflex KS084P is a reactor TPO (thermoplastic polyolefin) manufactured using LyondellBasell's proprietary Catalloy process technology. Adflex KS084P features a high melt flow and a low modulus. It is designed for many commercial and industrial extrusion applications. For regulatory compliance information, see the Adflex KS084P Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.890 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 30 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| Shore D, 15 sec | 35 | ASTM D2240, ISO 868 | |
| Shore A, 15 sec | 90 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 6.00 | MPa | |
| Break | 7.50 | MPa | |
| Tensile Strain (Break) | > 800 | % | ISO 527-2 |
| Flexural Modulus | 100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 3.0 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 40.0 | °C | ISO 75-2/B |
| Ductile / Brittle Transition Temperature | -55.0 | °C | ISO 6603-2 |
| Vicat Softening Temperature | 53.0 | °C | ISO 306/A50 |
| Melting Temperature | 164 | °C | DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stanyl® TS250F4D | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| AKROMID® S3 GF 15 1 natural (3223) | AKRO-PLASTIC GmbH | Nylon 610 | AKROMID® |
| Hostacom BG 722 AC BLACK | LyondellBasell Industries | PP Copolymer | Hostacom |
| TechnoMid PA6 S GK 30 | TechnoCompound GmbH | Nylon 6 | TechnoMid |
| CYCOLAC™ INP572 resin | SABIC Innovative Plastics | ABS+SAN | CYCOLAC™ |