| Nymax of nylon 6/6 polymers reinforced with glass fibers®GF 1200 series products are specially used in harsh environments and have the characteristics of high rigidity, tensile properties, heat resistance, durability, etc. According to the needs of rigid characteristics, these materials have a large range of strength and are easy to process in standard thermoplastic processing equipment. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.60 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 18600 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield 1 | 246 | MPa | ISO 527 |
| Fracture 2 | 214 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 2.0 - 3.0 | % | ASTM D638 |
| Flexural Modulus | |||
| -- | 15900 | MPa | ASTM D790 |
| -- 4 | 17100 | MPa | ISO 178 |
| Flexural Strength | 345 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, 3.18mm, injection molding | 130 | J/m | ASTM D256A |
| -- | 14 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 245 | °C | ISO 75-2 |
| 1.8 MPa, unannealed, 3.18mm | 250 | °C | ASTM D648 |
| Additional Information |
|---|
| Molded Test Bars: Dry as Molded |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Mold Temperature | 60.0 - 107 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| 3 . | Type 1, 5.1 mm/min |
| 4 . | 25 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wanthane® WHT-1195 | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |
| Zytel® HTN 51G35HSL BK083 | DuPont Performance Polymers | PPA | Zytel® HTN |
| Appeel® 2044 | DuPont Packaging & Industrial Polymers | EVA | Appeel® |
| Geon™ Vinyl Flexible B8000 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Karina RED COLOR CONCENTRATE 42/55-GE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |