NORYL™ ENG265F resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MhPK36_NORYL-ENG265F-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PPE+PS blend. Unfilled. Suitable for profile extrusion. NSF listed for potable water use in several colors (Standard 61). Low water absorption. Hydrolytic stability. Dimensional stability. Typical applications include tubes for reverse osmosis systems. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 8.5 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 8.70 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Water Absorption (24 hr) | 0.060 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2400 | MPa | ASTM D638 |
| -- | 2550 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 56.0 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2 |
| Fracture | 50.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation | |||
| Yield | 3.3 | % | ASTM D638 |
| Yield | 3.1 | % | ISO 527-2 |
| Fracture 3 | 28 | % | ASTM D638 |
| Fracture | 27 | % | ISO 527-2 |
| Flexural Modulus | |||
| 100mm span 4 | 2450 | MPa | ASTM D790 |
| 50.0mm span 5 | 2550 | MPa | ASTM D790 |
| -- | 2500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 95.0 | MPa | ISO 178 |
| Yield, 50.0mm span 6 | 89.0 | MPa | ASTM D790 |
| Yield, 100mm span 7 | 88.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/2C | ||
| -30°C | 10 | kJ/m² | ISO 179/2C |
| 23°C | 13 | kJ/m² | ISO 179/2C |
| Notched Izod Impact | |||
| -30°C | 110 | J/m | ASTM D256 |
| 23°C | 190 | J/m | ASTM D256 |
| -30°C 8 | 8.7 | kJ/m² | ISO 180/1A |
| 23°C 9 | 13 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 39.0 | J | ASTM D3763 |
| Dart Drop Impact | ASTM D3029 | ||
| -40°C | 5.42 | J | ASTM D3029 |
| -30°C | 25.8 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 132 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 6.40mm | 137 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 118 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 126 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 137 | °C | ISO 306/B50 |
| -- | 141 | °C | ISO 306/B120 |
| CLTE - Flow (-40 to 95°C) | 5.9E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 105 | °C | UL 746 |
| RTI Imp | 90.0 | °C | UL 746 |
| RTI | 105 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (3.20 mm, in Oil) | 20 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 2.65 | ASTM D150 | |
| 60 Hz | 2.65 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 4.0E-4 | ASTM D150 | |
| 60 Hz | 4.0E-4 | ASTM D150 | |
| Arc Resistance 10 | PLC 7 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.47 mm) | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 - 116 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Cylinder Zone 1 Temp. | 204 | °C | |
| Cylinder Zone 2 Temp. | 204 | °C | |
| Cylinder Zone 3 Temp. | 227 | °C | |
| Cylinder Zone 4 Temp. | 227 | °C | |
| Adapter Temperature | 249 | °C | |
| Melt Temperature | 227 - 254 | °C | |
| Die Temperature | 249 | °C |
| Extrusion instructions |
|---|
| Drying Time (Cumulative): 8 hrs |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.6 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Synres-Almoco DAIP 6502 | Synres-Almoco BV | DAP | Synres-Almoco |
| NEXT REGRIND PA6 8202-300RG | NEXT Specialty Resins, Inc. | Nylon 6 | NEXT REGRIND |
| Gallonprene® GP210-4011 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| DynaPath™ C1430CF | Polymer Dynamix | PBT | DynaPath™ |
| Lustran® 732 | INEOS Styrolution Group GmbH | ABS | Lustran® |