Fibremod™ K65G2
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Fibremod™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Mgyrcp_Fibremod-K65G2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fibremod K65G2 is a 20 % chemically coupled high performance glass fibre reinforced polypropylene compound intended for injection moulding. This material shows excellent mechanical properties also at elevated temperatures. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Vertical flow direction : 2.00mm | 1.0 | % | ISO 294-4 |
| Flow direction : 2.00mm | 0.20 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (1.00 mm) | 5500 | MPa | ISO 527-2 |
| Tensile Stress | 85.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 4600 | MPa | ISO 178 |
| Flexural Stress | 125 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 7.0 | kJ/m² | ISO 179/1eA |
| 23°C | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 25 | kJ/m² | ISO 179/1eU |
| 23°C | 45 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 9.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 160 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 145 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 165 | °C | ISO 306/A |
| -- | 132 | °C | ISO 306/B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Fogging 3(100°C) | 2.3 | mg | DIN 75201 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Feeding Temperatrue: 40 - 80 °CMass Temperature: 230 - 280 °CBack Pressure: Low to MediumScrew Speed: Low to MediumFlow Front Speed: 100 - 200 mm/s |
| Note Message | |
|---|---|
| 1 . | 150x80x2 |
| 2 . | 2.0 mm/min |
| 3 . | 16 h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Crastin® HR5315HF NC010 | DuPont Performance Polymers | PBT | Crastin® |
| Kumho SSBR SOL-C6450SL | Korea Kumho Petrochemical Co., Ltd. | SBR, Solution | Kumho SSBR |
| INSTRUC PSUGF30 | Infinity LTL Engineered Compounds | PSU | INSTRUC |
| Peripor® 300 E | BASF Corporation | PS (EPS) | Peripor® |
| Delene 5570 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TPE | Delene |