Hostaform® TF-10XAP®
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Hostaform® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Mgr2uk_Hostaform-TF-10XAP-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hostaform® acetal copolymer TF-10 XAP® is low emission, improved flow, impact modified grade providing optimum performance in general purpose injection molding primarily for the interior automotive market. This grade provides overall excellent performance with improved impact in many applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.38 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 13.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 1.9 | % | ISO 294-4 |
| Flow direction | 2.1 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1750 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 49.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 13 | % | ISO 527-2/1A/50 |
| Flexural Modulus (23°C) | 1700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | ISO 179/1eA |
| 23°C | 10 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 139 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 75.0 | °C | ISO 75-2/A |
| Melting Temperature 1 | 165 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 170 - 180 | °C | |
| Middle Temperature | 180 - 190 | °C | |
| Front Temperature | 180 - 190 | °C | |
| Nozzle Temperature | 180 - 200 | °C | |
| Processing (Melt) Temp | 180 - 200 | °C | |
| Mold Temperature | 80.0 - 100 | °C | |
| Injection Pressure | 60.0 - 120 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Holding Pressure | 60.0 - 120 | MPa | |
| Back Pressure | 0.00 - 0.500 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 190 to 200°CZone 4 Temperature: 180 to 200°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 D FR | RTP Company | Nylon 612 | RTP |
| Shin-Etsu Elastomer FE-371U | Shin-Etsu Silicones of America | Fluoro Si | Shin-Etsu Elastomer |
| 4DUR® 9K22120 S | 4Plas | PBT | 4DUR® |
| FHR Polypropylene 13R9A | Flint Hills Resources, LP | PP Random Copolymer | FHR Polypropylene |
| Hifax TYC 007P E C13097 | LyondellBasell Industries | PP Copolymer | Hifax |