RJM SL701M6T
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | RJM International, Inc. |
| Trademark: | RJM |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Mg5BDQ_RJM-SL701M6T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| RJM SL701M6T is a Polypropylene product filled with 30% talc. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Additive/Masterbatch. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.80 to 1.2 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 37.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 7.0 | % | ASTM D638 |
| Flexural Modulus | 3920 | MPa | ASTM D790 |
| Flexural Strength | 56.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 34 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | 140 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 180 to 220 | °C | |
| Mold Temperature | 60.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shuang-Bang AB-120 | Shuang-Bang Industrial Corp. | PUR, Unspecified | Shuang-Bang |
| Topolymer® 6211-H/G | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| Durepol® PBT A3 G30 PRTA011 BT304 MSP | Petropol Industry and Trade of Polymers LTDA | PBT | Durepol® PBT |
| OnForce™ LFT PP-60LGF/001 Natural | PolyOne Corporation | PP Homopolymer | OnForce™ LFT |
| ULTEM™ HU1010 resin | SABIC Innovative Plastics | PEI | ULTEM™ |