AKROMID® B28 GF 30 S3 natural (4835)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Mf40zP_AKROMID-B28-GF-30-S3-natural-4835-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B28 GF 30 S3 natural (4835) is a 30% glass fibre reinforced, dry impact resistant, easy flowing polyamide 6 with high stiffness and strength and light inherent color Applications are housings and covers for the automotive industry and power tools |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.30 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 35.0 | -- | cm³/10min | ISO 1133 |
| Humidity Absorption - 62% RH (70°C) | 2.1 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flexural Strain at Break 1 | 5.5 | -- | % | ISO 178 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 30 | -- | % | ISO 1172 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9000 | 4900 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 160 | 105 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 4.5 | 10 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 7500 | -- | MPa | ISO 178 |
| Flexural Stress 3 | 245 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 15 | -- | kJ/m² | |
| 23°C | 20 | 30 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 110 | -- | kJ/m² | |
| 23°C | 100 | 100 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 207 | -- | °C | ISO 75-2/A |
| Melting Temperature 4 | 220 | -- | °C | DIN EN 11357-1 |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10 K/min, DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2660 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Sylvin 8250-95 Natural | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Diakon® MG102K | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
| LNP™ THERMOCOMP™ HF008 compound | SABIC Innovative Plastics | Nylon 11 | LNP™ THERMOCOMP™ |
| PSM® HL-301B | Wuhan Huali Environmental Technology Co., Ltd. | TP, Unspecified | PSM® |