Promyde® B30 U
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | NUREL, S.A. |
| Trademark: | Promyde® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | McnFtl_Promyde-B30-U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Promyde B30 U is a Polyamide 6 flame retardant, UL certified, heat stabilised, nucleated and lubricated. CHARACTERISTICS Promyde B30 U is an improved flame retardant polyamide 6, UL certified, heat stabilized, lubricated and nucleated for fast cycle injection moulding. Its main characteristics are easy flowing, easy mould filling and very fast cooling time whilst maintaining excellent polyamide 6 mechanical properties. APPLICATIONS Due to its improved Glow Wire Flammability Index of 960°C, easy flow characteristics and very fast cooling time; Promyde B30 U is suitable for multi cavity and single cavity injection moulding of flame resistant parts such as components used in automotive, electrical, electronics, or technical parts. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.13 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 145 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ||||
| Vertical flow direction | 0.80 - 1.1 | -- | % | |
| Flow direction | 0.90 - 1.1 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 9.5 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 3.0 | -- | % | ISO 62 |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3300 | 1100 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 85.0 | 40.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 3.5 | 25 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | 18 | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 2800 | 1000 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 110 | 30.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | 30 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 187 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 65.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 3 | 222 | -- | °C | ISO 3146 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 80°C | 7.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 1.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.50 | 7.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.030 | 0.30 | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.50 mm) | V-2 | -- | UL 94 | |
| Glow Wire Flammability Index (1.50 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.50 mm) | 775 | -- | °C | IEC 60695-2-13 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | < 50.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Back Pressure: moderate |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VECTRA® T.rex541 | Celanese Corporation | LCP | VECTRA® |
| 4MID® 9A23300 | 4Plas | Nylon 66 | 4MID® |
| NOVADURAN® 5026 | Mitsubishi Engineering-Plastics Corp | PBT | NOVADURAN® |
| Formolene® HP3902 | Formosa Plastics Corporation, U.S.A. | MDPE | Formolene® |
| Huafon JF-P-8370AD / JF-I-5218 | Huafon Group Co., Ltd. | PUR-Ester | Huafon |