LNP™ LUBRICOMP™ 5CL24 compound
| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Mca5VG_LNP-LUBRICOMP-5CL24-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* 5CL24 is a compound based on Polyvinylidene Fluoride resin containing 10% PTFE and 20% Carbon Fiber. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound FP-VCL-4024 Product reorder name: 5CL24 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.78 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 17100 | MPa | ASTM D638 |
| Tensile Strength (Break) | 117 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.3 | % | ASTM D638 |
| Flexural Modulus | 14800 | MPa | ASTM D790 |
| Flexural Strength | 172 | MPa | ASTM D790 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 150 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 190 to 210 | °C | |
| Middle Temperature | 210 to 225 | °C | |
| Front Temperature | 225 to 245 | °C | |
| Processing (Melt) Temp | 215 to 230 | °C | |
| Mold Temperature | 65.0 to 90.0 | °C | |
| Back Pressure | 0.170 to 0.340 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® 5430 | Chevron Phillips Chemical Company LLC | LDPE | MarFlex® |
| S&E Wire & Cable GA-2190E-FR CLEAR | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Wire & Cable |
| Altuglas® DR FROSTED | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Altuglas® |
| K-Prene XL-A40 | Technovinyl Polymers India Ltd. | PP+EPDM | K-Prene |
| FHR Polypropylene AP4135-LV | Flint Hills Resources, LP | PP Impact Copolymer | FHR Polypropylene |