SUMIKASUPER® LCP E5002L
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Sumitomo Chemical Co., Ltd. |
| Trademark: | SUMIKASUPER® LCP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | McGmb3_SUMIKASUPER-LCP-E5002L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SUMIKASUPER LCP is a thermotropic liquid crystalline polyester, showing the highest heat resistance among engineering plastics. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.070 | % | |
| Across Flow | 1.3 | % | |
| Water Absorption (Saturation) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 150 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.7 | % | ASTM D638 |
| Flexural Modulus (23°C) | 9510 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C) | 127 | MPa | ASTM D790 |
| Poisson's Ratio | 0.51 | ASTM E132 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.40 mm) | 180 | J/m | ASTM D256 |
| Unnotched Izod Impact (6.40 mm) | 480 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 354 | °C | ASTM D648 |
| CLTE | Internal Method | ||
| Flow : 150°C | 2.0E-6 | cm/cm/°C | |
| Transverse : 150°C | 8.1E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.44 | W/m/K | JIS R2618 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Constant | ASTM D150 | ||
| 1 MHz | 3.40 | ||
| 1.00 GHz | 3.10 | ||
| Dissipation Factor | ASTM D150 | ||
| 1 MHz | 0.023 | ||
| 1.00 GHz | 4.0E-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.300 mm, All colors) | V-0 | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Soldering Resistance | 350 | °C | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 | °C | |
| Drying Time | 4.0 to 24 | hr | |
| Rear Temperature | 350 to 370 | °C | |
| Middle Temperature | 370 to 390 | °C | |
| Front Temperature | 390 to 410 | °C | |
| Nozzle Temperature | 390 to 410 | °C | |
| Processing (Melt) Temp | 400 | °C | |
| Mold Temperature | 40.0 to 160 | °C | |
| Injection Pressure | 120 to 160 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 40.0 to 60.0 | MPa | |
| Back Pressure | 1.00 to 5.00 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3640 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RTP 4099 X 128641 A | RTP Company | PPA | RTP |
| Witcom POM-C 2012/300 EXP2 | Witcom Engineering Plastics B.V. | Acetal (POM) Copolymer | Witcom POM-C |
| Generic Cellulose, Regenerated | Generic | Cellulose, Regenerated | Generic |
| ENFLEX V1080A BLK UV | ENPLAST Americas, a Ravago Group Company | TPV | ENFLEX |