ELITE™ NG 5400B
| Category: | EPE , Enhanced Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ELITE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Mc1zuL_ELITE-NG-5400B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ELITE™ NG 5400B is a Linear Low Density Polyethylene, 1-Octene copolymer, produced with the SOLUTION™ technology. This resin presents excellent tensile, tear and puncture resistance even at low temperatures with great gloss and clarity. It has a low seal initiation temperature with high seal performance. Main Characteristics:
|
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.916 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Film Puncture Resistance (38 µm) | 10.0 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 38 µm | 134 | MPa | ASTM D882 |
| 2% secant, TD : 38 µm | 143 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm | 10.0 | MPa | ASTM D882 |
| TD : Yield, 38 µm | 10.0 | MPa | ASTM D882 |
| MD : Fracture, 38 µm | 40.0 | MPa | ASTM D882 |
| TD : Fracture, 38 µm | 36.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 38 µm | 750 | % | ASTM D882 |
| TD : Fracture, 38 µm | 930 | % | ASTM D882 |
| Dart Drop Impact (38 µm) | 1400 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm | 700 | g | ASTM D1922 |
| TD : 38 µm | 910 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 37.5 µm) | 64 | ASTM D2457 | |
| Haze (37.5 µm) | 9.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 232 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的加工条件： 螺杆直径：63.5 mm（2.5 英寸）；24.5 L/D 模具间隙：1.8 mm（70 密尔） 熔体温度： 232°C (450°F) 输出：52 kg/h（113 磅/小时） 模具直径：152 mm（6 英寸） 放大比：2.5:1 螺杆速度：83 rpm 冷冻线高度：635 mm（25 英寸） |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RX® 1-501N | Sumitomo Bakelite North America, Inc. | DAP | RX® |
| Menzolit® HPC 1300 | Menzolit Ltd (UK) | Polyester, TS | Menzolit® |
| DOW™ Electrical & Telecommunications DHDA-7707 BK | The Dow Chemical Company | Polyolefin, Unspecified | DOW™ Electrical & Telecommunications |
| GELOY™ XTWE265 resin | SABIC Innovative Plastics Asia Pacific | ASA | GELOY™ |
| Hostaform® C 13021 XAP² ™ LS colored | Celanese Corporation | PPS | Hostaform® |