Generic Nylon 612 - Carbon Fiber
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MboGqO_Generic-Nylon-612---Carbon-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 612 - Carbon Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 - 1.55 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (23°C) | 0.10 - 0.30 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.10 - 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 6550 - 27600 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 123 - 207 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 2.0 - 2.5 | % | ASTM D638 |
| Fracture, 23°C | 1.0 - 2.3 | % | ASTM D638 |
| Flexural Modulus (23°C) | 5510 - 22400 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 188 - 334 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 43 - 120 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 300 - 960 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 210 - 221 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 197 - 219 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0 - 2.5E+4 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.2 - 79.5 | °C | |
| Drying Time | 3.9 - 4.1 | hr | |
| Rear Temperature | 259 - 268 | °C | |
| Middle Temperature | 265 - 269 | °C | |
| Front Temperature | 265 - 277 | °C | |
| Processing (Melt) Temp | 267 - 274 | °C | |
| Mold Temperature | 76.5 - 79.7 | °C | |
| Injection Pressure | 95.7 - 103 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 612 - Carbon FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA III HDPERBI 8.0 | ROMPETROL PETROCHEMICALS S.R.L. | HDPE | MIDILENA III |
| CYCOM® 5250-4 RTM | Cytec Industries Inc. | MAH-g | CYCOM® |
| Kemcor HD 0892 | Qenos Pty Ltd | HDPE, HMW | Kemcor |
| OmniLon™ PA6/6 U GR25 BK1000 | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |
| Paxon™ BA53-055 | ExxonMobil Chemical | HDPE, UHMW | Paxon™ |