KEBAFORM® C 904 CF
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | BARLOG plastics GmbH |
| Trademark: | KEBAFORM® C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MaAXD2_KEBAFORM-C-904-CF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POM Copolymer, carbon fiber reinforced, electr. conductive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.46 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.5 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 15000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 115 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.5 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 162 | °C | ISO 75-2/A |
| Melting Temperature 1 | 166 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+6 | ohms·cm | IEC 60093 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ExxonMobil™ PP5032E3 | ExxonMobil Chemical | PP Homopolymer | ExxonMobil™ |
| Fainplast PVC GSK 6635 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Ducor® 2640 RC | Ducor Petrochemicals BV | PP Impact Copolymer | Ducor® |
| Edgetek™ AT-000/000 NC707 | PolyOne Corporation | Acetal (POM) Copolymer | Edgetek™ |
| Polychim HL10XF | Polychim Industrie S.A.S. | PP Homopolymer | Polychim |