DIC.PPS AMORVON® W-30
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | DIC Corporation |
| Trademark: | DIC.PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MZZQWC_DIC-PPS-AMORVON-W-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.57 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.25 | % | |
| Across Flow | 1.0 | % | |
| Water Absorption (23°C, 24 hr) | 0.060 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 100 | ||
| R-Scale | 121 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11000 | MPa | ASTM D638 |
| Tensile Strength | 160 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.7 | % | ASTM D638 |
| Flexural Modulus | 10000 | MPa | ASTM D790 |
| Flexural Strength | 220 | MPa | ASTM D790 |
| Compressive Strength | 180 | MPa | ASTM D695 |
| Poisson's Ratio | 0.37 | ||
| Coefficient of Friction | ASTM D1894 | ||
| vs. Steel - Dynamic | 0.35 | ||
| vs. Steel - Static | 0.35 | ||
| Flexural Elongation at Break | 2.2 | % | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 65 | J/m | ASTM D256 |
| Unnotched Izod Impact | 480 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 230 | °C | ASTM D648 |
| CLTE | ASTM D696 | ||
| Flow : -30 to 90°C | 2.3E-5 | cm/cm/°C | |
| Transverse : -30 to 90°C | 2.3E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 16 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.00 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 2.0E-3 | ASTM D150 | |
| Arc Resistance | 120 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 300 to 340 | °C | |
| Middle Temperature | 300 to 340 | °C | |
| Front Temperature | 300 to 340 | °C | |
| Mold Temperature | 120 to 150 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Styropor® P-240AH | BASF Corporation | PS (EPS) | Styropor® |
| Witcom PA6 5G-AS-S | Witcom Engineering Plastics B.V. | Nylon 6 | Witcom PA6 |
| Alkathene® Ultra LDH210 | Qenos Pty Ltd | LLDPE | Alkathene® Ultra |
| ExxonMobil™ LLDPE LL 6101 Series | ExxonMobil Chemical | LLDPE | ExxonMobil™ LLDPE |
| Petrothene® NA345009 | LyondellBasell Industries | LDPE | Petrothene® |