LNP LUBRICOMP MFL36S is a compound based on Polypropylene resin containing Glass Fiber, PTFE. Added features of this material include: Heat Stabilized. Also known as: LNP* LUBRICOMP* Compound MFXL4036HS Product reorder name: MFL36S |
General Information | |
---|---|
Filler / Reinforcement |
|
Additive |
|
Features |
|
RoHS Compliance |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Density | 1.26 | g/cm³ | ISO 1183 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Modulus | 6900 | MPa | ISO 527-2/1 |
Tensile Stress (Break) | 85.0 | MPa | ISO 527-2/5 |
Tensile Strain (Break) | 2.8 | % | ISO 527-2/5 |
Flexural Modulus 1 | 6400 | MPa | ISO 178 |
Flexural Stress | 123 | MPa | ISO 178 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact 2(23°C) | 10 | kJ/m² | ISO 180/1A |
Unnotched Izod Impact Strength 3(23°C) | 50 | kJ/m² | ISO 180/1U |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Linear thermal expansion coefficient | ISO 11359-2 | ||
Flow : 23 to 60°C | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
Lateral : 23 to 60°C | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
Note Message | |
---|---|
1 . | 2.0 mm/min |
2 . | 80*10*4 |
3 . | 80*10*4 |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
AGRIPLAS™ BFF3015H | A. Schulman Inc. | PP, Unspecified | AGRIPLAS™ |
Fainplast PVC KL 92/3 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
Exelene® HDPE 4000 | Montachem International, Inc. | HDPE | Exelene® HDPE |
ENFLEX V1030A | ENPLAST Americas, a Ravago Group Company | TPV | ENFLEX |
Karina CRYSTAL PVC COMPOUND -E 75/201-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Rigid | Karina |