Borealis PP SD233CF
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MYqyI6_Borealis-PP-SD233CF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SD233CF is a very soft random heterophasic copolymer. This grade is suitable for the manufacturing of unoriented films on chill roll processes. CAS-No. 9010-79-1 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 500 | MPa | ISO 178 |
| Coefficient of Friction | > 0.70 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-3 | ||
| MD | 300 | MPa | |
| TD | 300 | MPa | |
| Tensile Strength | ISO 527-3 | ||
| MD | 40.0 | MPa | |
| TD | 30.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break | 600 | % | |
| TD : Break | 700 | % | |
| Instrumented Dart Impact (Total Energy) | 35.0 | J | ISO 7765-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 140 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°) | > 100 | ASTM D2457 | |
| Haze | < 4.0 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMLLOY PBB701 | Polyram Ram-On Industries | PC+ABS | RAMLLOY |
| Akulon® K224-PG3 | DSM Engineering Plastics | Nylon 6 | Akulon® |
| Amodel® AT-1125 HS | Solvay Specialty Polymers | PPA | Amodel® |
| Sylvin 9604-80 CLEAR 8159 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NORYL™ FE1520PW resin | SABIC Innovative Plastics Europe | PPE+PS | NORYL™ |