RODRUN LC-5000
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | UNITIKA Plastics Division |
| Trademark: | RODRUN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MYlFMX_RODRUN-LC-5000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Unitika Rodrun is a thermoplastics for percision injection classified into semi-aromatic liquid crystal polyesters (LCPs). LC-5000 series has a excellent moldability (high flow without flash, using a mold of low temperature) and precision (low warpage). LC-5000 series are suitable for almost all dipping soldering conditions and partial reflow soldering (low warpage). LCP has stiff molecular structure to form liquid crystal at molten stage. The archeological properties of low viscosity under shear stress gives high flow without flash problems. Rodrun which use a standard mold temperature of 40°C shows the rheological merit of LCP clearly. Out shape of a LCP seem to be just like a normal plastics, however, the solid LCP consists of crystal and glasified liquid crystal. Rodrun has a low crystalinity in the mold. This property yields low shrinkage and low warpage. Rodrun is a suitable resin for precision parts. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Water Absorption (23°C, 24 hr) | 0.010 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 3.20 mm) | 176 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.4 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1.60 mm | 13200 | MPa | |
| 3.20 mm | 9800 | MPa | |
| Flexural Strength | ASTM D790 | ||
| Yield, 1.60 mm | 142 | MPa | |
| Yield, 3.20 mm | 137 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | 230 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 210 | °C | |
| 1.8 MPa, Unannealed | 170 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-2 | ||
| 3.20 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 | °C | |
| Drying Time | 4.0 | hr | |
| Hopper Temperature | 120 | °C | |
| Rear Temperature | 270 | °C | |
| Middle Temperature | 280 | °C | |
| Front Temperature | 290 | °C | |
| Nozzle Temperature | 290 | °C | |
| Mold Temperature | 40.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NILENE® E8 | Taro Plast S.p.A. | PP Copolymer | NILENE® |
| Exelene® PET IV 84 FR | Montachem International, Inc. | PET | Exelene® PET |
| ADENE® O07MFBG-00 | A.D. Compound S.p.A. | PP Copolymer | ADENE® |
| Elastocon® 9050B | Elastocon TPE Technologies | TPE | Elastocon® |
| Kynar Flex® 3030-10 | Arkema | PVDF | Kynar Flex® |