KOCETAL® CB301
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Kolon Plastics, Inc. |
| Trademark: | KOCETAL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MYW2Mq_KOCETAL-CB301.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Kocetal CB301 is carbon black reinforced electric conductive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.9 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 60%RH) | 0.22 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 75 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 55.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 20 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2400 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 83.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 152 | °C | |
| 1.8 MPa, Unannealed | 106 | °C | |
| Melting Temperature | 166 | °C | |
| CLTE - Flow | 1.3E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+2 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | > 3.0 | hr | |
| Suggested Max Regrind | 30 | % | |
| Rear Temperature | 170 to 190 | °C | |
| Middle Temperature | 190 to 210 | °C | |
| Front Temperature | 200 to 220 | °C | |
| Nozzle Temperature | 200 to 220 | °C | |
| Processing (Melt) Temp | 165 to 220 | °C | |
| Mold Temperature | 70.0 to 120 | °C | |
| Injection Pressure | 98.1 | MPa | |
| Holding Pressure | 29.4 to 49.0 | MPa | |
| Back Pressure | 1.96 to 4.90 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4295 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Adsyl 3 C 30 F HP | LyondellBasell Industries | Polyolefin, Unspecified | Adsyl |
| EMPILON® 610 | EMPILON | SEBS | EMPILON® |
| Jampilen HP550J | Jam Polypropylene Company | PP Homopolymer | Jampilen |
| LNP™ FARADEX™ MS003 compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ FARADEX™ |