Shinko-Lac® ABS TM25
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Mitsubishi Rayon America Inc. |
| Trademark: | Shinko-Lac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MXxa9Q_Shinko-Lac-ABS-TM25.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Shinko-Lac® ABS TM25 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in North America. Primary attribute of Shinko-Lac® ABS TM25: Flame Rated. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 0.30 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 108 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 44.1 | MPa | ASTM D638 |
| Flexural Modulus (23°C, 6.35 mm) | 2350 | MPa | ASTM D790 |
| Flexural Strength (23°C, 6.35 mm) | 71.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 170 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 102 | °C | ASTM D648 |
| Vicat Softening Temperature | 117 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RELENE® F19010 | Reliance Industries Limited | LLDPE | RELENE® |
| Spartech Polycom SC7F-7015U | Spartech Polycom | PC | Spartech |
| Nylene® NX4797 | Custom Resins Group | Nylon 6 | Nylene® |
| Geon™ HTX M6829 | PolyOne Corporation | PVC Alloy | Geon™ HTX |
| CYCOLOY™ RCX7243 resin | SABIC Innovative Plastics Asia Pacific | PC | CYCOLOY™ |