ALCOM®AWL 113/15 WT1013-12LB is a polycarbonate + acrylonitrile butadiene styrene (PC + ABS) product, which contains 15% filler. It can be processed by injection molding and is available in North America, Europe or the Asia-Pacific region. ALCOM®AWL 113/15 WT1013-12LB applications include mirrors, automotive industry and lighting equipment. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 15.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 117 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 48.0 | MPa | ISO 527-2 |
| Fracture | 40.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 3.0 | % | ISO 527-2 |
| Fracture | 12 | % | ISO 527-2 |
| Flexural Modulus | 2700 | MPa | ISO 178 |
| Flexural Stress | 79.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 90 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 100 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 113 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm | HB | UL 94 | |
| 3.0 mm | HB | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tristimulus Value | |||
| Y10 of Reflection | 92 | % | DIN 5033 |
| Y10 of Transmission : 500.0 µm | 0.40 | % | ISO 13468 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| Dehumidification desiccant | 80 - 90 | °C | |
| Hot air dryer | 80 - 90 | °C | |
| Drying Time | |||
| Dehumidification desiccant | 3.0 - 6.0 | hr | |
| Hot air dryer | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 230 - 260 | °C | |
| Mold Temperature | 50 - 80 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex AT0110GN | Ginar Technology Co., LTD. | Nylon 66 | Mapex |
| Talcoprene® 1530TC NATURALE | SO.F.TER. SPA | PP, Unspecified | Talcoprene® |
| Texalan® 3 Series 390A | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 3 Series |
| DESLON™ 6 DSC102G9 | DESCO Co., Ltd. | Nylon 6 | DESLON™ 6 |
| LNP™ THERMOCOMP™ LC006 compound | SABIC Innovative Plastics | PEEK | LNP™ THERMOCOMP™ |