Generic TPU, Unspecified
| Category: | TPU, Unspecified , Thermoplastic Polyurethane Elastomer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MXTe7N_Generic-TPU-Unspecified.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic TPU, Unspecified This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.978 - 1.43 | g/cm³ | ASTM D792 |
| 23°C | 0.938 - 1.22 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.80 - 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow (23°C) | 0.35 - 3.7 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.020 - 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 50 - 110 | ASTM D785 | |
| Durometer Hardness | |||
| 23°C | 40 - 95 | ASTM D2240 | |
| 23°C | 40 - 97 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1450 - 2330 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield, 23°C | 8.27 - 76.5 | MPa | ASTM D638 |
| Fracture, 23°C | 4.14 - 65.5 | MPa | ASTM D638 |
| Fracture, 23°C | 18.3 - 50.0 | MPa | ISO 527-2 |
| 23°C | 1.31 - 12.9 | MPa | ASTM D638 |
| 23°C | 2.00 - 32.2 | MPa | ISO 527-2 |
| Tensile Stress (23°C) | 2.47 - 16.1 | MPa | ASTM D1708 |
| Tensile Elongation | |||
| Fracture, 23°C | 20 - 580 | % | ASTM D638 |
| Fracture, 23°C | 430 - 1100 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 22.1 - 79.9 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 1.45 - 83.0 | MPa | ASTM D790 |
| Taber Abrasion Resistance (23°C) | 5.40 - 85.1 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| 100% strain, 23°C | 0.827 - 7.01 | MPa | ASTM D412 |
| 100% strain, 23°C | 0.900 - 16.0 | MPa | ISO 37 |
| 300% strain, 23°C | 2.07 - 29.6 | MPa | ASTM D412 |
| 300% strain, 23°C | 9.00 - 25.3 | MPa | ISO 37 |
| Tensile Strength | |||
| Yield, 23°C | 2.50 - 25.2 | MPa | ASTM D412 |
| Yield, 23°C | 13.8 - 30.4 | MPa | ISO 37 |
| Fracture, 23°C | 6.00 - 41.1 | MPa | ASTM D412 |
| Tensile Elongation | |||
| Fracture, 23°C | 190 - 1200 | % | ASTM D412 |
| Fracture, 23°C | 450 - 980 | % | ISO 37 |
| Tear Strength | |||
| 23°C | 19.3 - 136 | kN/m | ASTM D624 |
| 23°C | 26 - 150 | kN/m | ISO 34-1 |
| Compression Set | |||
| -- | 13 - 70 | % | ASTM D395 |
| 23°C | 18 - 53 | % | ISO 815 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 260 - 870 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 71.9 - 79.4 | °C | ASTM D648 |
| Glass Transition Temperature | -67.0 - 79.0 | °C | ASTM E1356 |
| Vicat Softening Temperature | 66.7 - 105 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.8 - 113 | °C | |
| Drying Time | 1.5 - 10 | hr | |
| Suggested Max Moisture | 0.010 - 0.030 | % | |
| Rear Temperature | 164 - 241 | °C | |
| Middle Temperature | 160 - 246 | °C | |
| Front Temperature | 169 - 248 | °C | |
| Nozzle Temperature | 170 - 254 | °C | |
| Processing (Melt) Temp | 171 - 247 | °C | |
| Mold Temperature | 20.0 - 74.0 | °C | |
| Injection Pressure | 6.00 - 103 | MPa | |
| Back Pressure | 0.433 - 5.52 | MPa | |
| Screw Speed | 50 - 60 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic TPU, UnspecifiedThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 48.4 - 113 | °C | |
| Drying Time | 1.5 - 5.0 | hr | |
| Cylinder Zone 1 Temp. | 149 - 238 | °C | |
| Cylinder Zone 3 Temp. | 159 - 233 | °C | |
| Cylinder Zone 5 Temp. | 180 - 233 | °C | |
| Melt Temperature | 189 - 230 | °C | |
| Die Temperature | 188 - 235 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic TPU, UnspecifiedThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Small Boss SPVC8011 | Tongxiang Small Boss Special Plastic Products Co., Ltd. | PVC, Unspecified | Small Boss |
| LAMIGAMID® 324/327 | Schwartz Technical Plastic | Nylon 6 | LAMIGAMID® |
| PENTAMID A GV30 H red 3000/2 | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |
| ENFLEX VU-420-90A | ENPLAST, a Ravago Group Company | PP+EPDM | ENFLEX |
| Durethan® AKV 15 FN 00 000000 | LANXESS GmbH | Nylon 66 | Durethan® |