SCLAIR® 17A
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | NOVA Chemicals |
| Trademark: | SCLAIR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MWqEHX_SCLAIR-17A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SCLAIR® 17A is a High Density Polyethylene material. It is available in North America for coextrusion. Important attributes of SCLAIR® 17A are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.950 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.45 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 67 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 0.24 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 38 µm | 630 | MPa | |
| 1% Secant, TD : 38 µm, Blown Film | 900 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm, Blown Film | 22.0 | MPa | |
| TD : Yield, 38 µm, Blown Film | 20.0 | MPa | |
| MD : Break, 38 µm, Blown Film | 45.0 | MPa | |
| TD : Break, 38 µm, Blown Film | 20.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 38 µm, Blown Film | 650 | % | |
| TD : Break, 38 µm, Blown Film | 750 | % | |
| Dart Drop Impact (38 µm, Blown Film) | 40 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, Blown Film | 22 | g | |
| TD : 38 µm, Blown Film | 880 | g | |
| Nitrogen Transmission Rate (73°C, 38 µm, Blown Film, 0.0% RH) | 1920 | cm³/m²/24 hr | ASTM D1434 |
| Water Vapor Transmission Rate (38°C, 100% RH, 38 µm, Blown Film) | 4.0 | g/m²/24 hr |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 125 | °C | ASTM D1525 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Low Friction Puncture - Blown Film (38.0 µm) | 230 | J/cm | Internal Method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9717-65 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Trademark PE mLLD1918F | Trademark Plastics Corporation | mLLDPE | Trademark PE |
| ESENTTIA 03R45C | Polipropileno del Caribe S.A. | PP Random Copolymer | ESENTTIA |
| Plaslube® PA6/6 GF12 TL20 | Techmer Engineered Solutions | Nylon 66 | Plaslube® |
| Sylvin 8260-75UV Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |