Ingeo™ 3100HP
| Category: | PLA , Polylactic Acid |
| Manufacturer: | NatureWorks® LLC |
| Trademark: | Ingeo™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MWnefq_Ingeo-3100HP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ingeo 3100HP is a medium viscosity product from NatureWorks LLC, designed for medium flow injection molding applications. It is designed to crystallize during processing, leading to higher heat deflection temperatures in opaque applications. The variety of products made with 3100HP is widely varied and growing. Applications include disposables such as cutlery, cups, plates, cosmetic packaging, and durables such as electronics housings and semi-durable building materials. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (210°C/2.16 kg) | 24 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | |||
| -- 1 | 1.7 - 1.8 | % | |
| -- 2 | 0.20 - 0.40 | % | |
| Relative Viscosity 3 | 3.1 | ASTM D5225 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield 4 | 64.1 | MPa | ASTM D638 |
| Yield 5 | 64.8 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Fracture 6 | 2.2 | % | ASTM D638 |
| Fracture 7 | 3.4 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| -- 8 | 4360 | MPa | ASTM D790 |
| -- 9 | 3590 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| -- 10 | 108 | MPa | ASTM D790 |
| -- 11 | 112 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -- 12 | 32 | J/m | ASTM D256 |
| -- 13 | 18 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM E2092 | ||
| 0.45 MPa, not annealed 14 | 149 | °C | ASTM E2092 |
| 0.45 MPa, not annealed 15 | 54.0 | °C | ASTM E2092 |
| Peak Crystallization Temperature (DSC) 16 | 180 | °C |
| Optical | Nominal Value | ||
|---|---|---|---|
| Clarity | |||
| -- 17 | Opaque | ||
| -- 18 | Transparent |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | < 0.025 | % | |
| Hopper Temperature | 21.1 | °C | |
| Rear Temperature | 185 | °C | |
| Middle Temperature | 195 | °C | |
| Front Temperature | 200 | °C | |
| Nozzle Temperature | 200 | °C | |
| Processing (Melt) Temp | 199 | °C | |
| Mold Temperature | 120 | °C | |
| Back Pressure | 1.72 | MPa | |
| Screw Speed | 200 | rpm |
| Injection instructions |
|---|
| Note: Amorphous polymer must be dried below 120F (50C). |
| Note Message | |
|---|---|
| 1 . | Molded crystalline with 120°C mold temperature where formula included 1wt% nucleating agent (LAK-301 from Takemoto Oil & Fat) |
| 2 . | Molded amorphous with 26°C mold temperature |
| 3 . | Measured at 1.0 g/dL in chloroform at 30°C |
| 4 . | Molded crystalline with 120°C mold temperature where formula included 1wt% nucleating agent (LAK-301 from Takemoto Oil & Fat) |
| 5 . | Molded amorphous with 26°C mold temperature |
| 6 . | Molded crystalline with 120°C mold temperature where formula included 1wt% nucleating agent (LAK-301 from Takemoto Oil & Fat) |
| 7 . | Molded amorphous with 26°C mold temperature |
| 8 . | Molded crystalline with 120°C mold temperature where formula included 1wt% nucleating agent (LAK-301 from Takemoto Oil & Fat) |
| 9 . | Molded amorphous with 26°C mold temperature |
| 10 . | Molded crystalline with 120°C mold temperature where formula included 1wt% nucleating agent (LAK-301 from Takemoto Oil & Fat) |
| 11 . | Molded amorphous with 26°C mold temperature |
| 12 . | Molded crystalline with 120°C mold temperature where formula included 1wt% nucleating agent (LAK-301 from Takemoto Oil & Fat) |
| 13 . | Molded amorphous with 26°C mold temperature |
| 14 . | Molded crystalline with 120°C mold temperature where formula included 1wt% nucleating agent (LAK-301 from Takemoto Oil & Fat) |
| 15 . | Molded amorphous with 26°C mold temperature |
| 16 . | Molded crystalline with 120°C mold temperature where formula included 1wt% nucleating agent (LAK-301 from Takemoto Oil & Fat) |
| 17 . | Molded crystalline with 120°C mold temperature where formula included 1wt% nucleating agent (LAK-301 from Takemoto Oil & Fat) |
| 18 . | Molded amorphous with 26°C mold temperature |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RapidVac™ VA-1610 | Innovative Polymers, Inc. | TSU | RapidVac™ |
| AIE PC/ABS A2200HF-T5 | Asia International Enterprise (Hong Kong) Limited | PC+ABS | AIE PC/ABS |
| Elexar® EL-8614 | Teknor Apex Company | TPE | Elexar® |
| Hostacom HBG H01 NAT | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Moplen HP525J | PolyMirae | PP Homopolymer | Moplen |