XENOY™ X4820 resin
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | XENOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MVxdwh_XENOYX4820resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| XENOY X4820 is a high modulus PC/PBT Blend. This resin provides high chemical resistance, excellent impact, very low creep, low CTE, excellent fatigue and dimensional stability. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.25 | g/cm³ | ASTM D792 |
| -- | 1.26 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 10 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (265°C/5.0 kg) | 12.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.95 - 1.1 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.42 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.14 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3200 | MPa | ASTM D638 |
| -- | 3000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 57.0 | MPa | ASTM D638 |
| Yield | 58.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 58.0 | MPa | ASTM D638 |
| Fracture | 52.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 4.2 | % | ASTM D638 |
| Yield | 4.2 | % | ISO 527-2/50 |
| Fracture 5 | 140 | % | ASTM D638 |
| Fracture | 100 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2900 | MPa | ASTM D790 |
| -- 7 | 2850 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 87.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 91.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 60 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 150 | J/m | ASTM D256 |
| 23°C | 700 | J/m | ASTM D256 |
| -30°C 10 | 15 | kJ/m² | ISO 180/1A |
| 23°C 11 | 55 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 60.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 98.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 12 | 94.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 130 | °C | ASTM D1525 13 |
| -- | 132 | °C | ISO 306/B50 |
| -- | 134 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 1.1E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 50 - 80 | % | |
| Rear Temperature | 238 - 260 | °C | |
| Middle Temperature | 243 - 266 | °C | |
| Front Temperature | 249 - 271 | °C | |
| Nozzle Temperature | 249 - 266 | °C | |
| Processing (Melt) Temp | 254 - 277 | °C | |
| Mold Temperature | 37.8 - 87.8 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 80 | rpm | |
| Vent Depth | 0.013 - 0.020 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Royalcast® 2505 | Chemtura | PUR-Ether | Royalcast® |
| Tecotek® BC40 UF45 NL CE | Eurotec Engineering Plastics | PC+ABS | Tecotek® |
| Fainplast PVC PH 50/AM-UV | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Edgetek™ PA6-GL30 BK010 | PolyOne Corporation | Nylon 6 | Edgetek™ |
| Hifax TYC 1168P | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |