SHINSTRA WG30TKB
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Shinil Chemical Industry Co., Ltd. |
| Trademark: | SHINSTRA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MVqG9i_SHINSTRAWG30TKB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SHINSTRA is our flagship product - provide improved modulus, impact resistance and heat resistance which are the weak points of plastic materials. Generally, SHINSTRA satisfy requirements by customizing (1) impact resistance, (2) scratch resistance, (3) abrasion, (4) chemical resistance, (5) processability and (6) heat resistance. In addition to the excellent products, we are offering total solution optimizing product designand customer's process lines through Computer Aided Engineering (CAE). SHINSTRA can be produced with PC, HIPS, PE, PP, PA-6 and PA-6,6 in our proprietary dispersion technology and used in many applications such as exterior and interior auto parts, home appliance and construction materials. APPLICATION: cylinder head cover |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.30 - 0.70 | % | Internal method |
| Moisture Content | 0.040 | % | ISO 15512 |
| Ash Content | 27 - 33 | % | ISO 3451-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9600 | MPa | ISO 527-2/5 |
| Tensile Stress (Break) | 175 | MPa | ISO 527-2/5 |
| Flexural Modulus 1 | 8500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | ISO 179/1eA |
| 23°C | 8.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ISO 180/1A | ||
| -40°C | 7.0 | kJ/m² | ISO 180/1A |
| 23°C | 9.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 245 | °C | ISO 75-2/A |
| Melting Temperature (DSC) 2 | 260 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 3 | 1.0E+14 | ohms | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Processing (Melt) Temp | 270 - 290 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 10°C/min |
| 3 . | 23°C/50% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quantum Composites QC-8704 | Quantum Composites Inc. | Vinyl Ester | Quantum Composites |
| Trademark PE LLB1918C | Trademark Plastics Corporation | LLDPE | Trademark PE |
| Xuchuan XCW-6022NB | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Dorlyl PVC FC 37B | DORLYL S.N.C. | PVC, Unspecified | Dorlyl PVC |
| LNP™ LUBRICOMP™ RX01514 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |