Ultradur® S 4090 G4 BK5110
| Category: | PBT+ASA , Polybutylene Terephthalate + ASA |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultradur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MUyPzd_Ultradur-S-4090-G4-BK5110.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultradur S 4090 G4 BK5110 is a 20% glass reinforced, pigmented black PBT+ASA blend. It produces moldings with good surface finish, is resistant to chemicals and stress cracking, and has low shrinkage and warpage. Applications Applications include highly stressed equipment housings in the automotive, electrical and household sectors. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.39 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 20.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.74 | % | |
| Flow | 0.43 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.40 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 6900 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Break, -40°C | 160 | MPa | |
| Break, 23°C | 100 | MPa | |
| Break, 80°C | 68.0 | MPa | |
| Break, 121°C | 42.0 | MPa | |
| Tensile Strain (Break, 23°C) | 2.5 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 6400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 43 | kJ/m² | |
| 23°C | 55 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | 7.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 205 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 160 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 223 | °C | ISO 3146 |
| CLTE - Flow | 4.0E-5 | cm/cm/°C | |
| RTI Elec | UL 746 | ||
| 0.710 mm | 130 | °C | |
| 1.50 mm | 130 | °C | |
| 3.00 mm | 130 | °C | |
| RTI Imp | UL 746 | ||
| 0.710 mm | 90.0 | °C | |
| 1.50 mm | 90.0 | °C | |
| 3.00 mm | 90.0 | °C | |
| RTI Str | UL 746 | ||
| 0.710 mm | 130 | °C | |
| 1.50 mm | 130 | °C | |
| 3.00 mm | 130 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Constant | IEC 60250 | ||
| 100 Hz | 3.70 | ||
| 1 MHz | 3.60 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 3.0E-3 | ||
| 1 MHz | 0.019 | ||
| Comparative Tracking Index | 450 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.710 mm | HB | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | < 1.00 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax 6301 | LyondellBasell Industries | PP Homopolymer | Pro-fax |
| ETILINAS BPD 4045 | POLYETHYLENE MALAYSIA SDN BHD | HDPE | ETILINAS |
| Hanwha Total PP BJ750 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Impact Copolymer | Hanwha Total PP |
| Hylon® N1000HL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| Lucky Enpla LPB1000 | Lucky Enpla Co LTD | PBT | Lucky Enpla |