VALOX™ 310 resin

Category:	PBT , Polybutylene Terephthalate
Manufacturer:	SABIC Innovative Plastics
Trademark:	VALOX™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	MUXpMM_VALOX-310-resin.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
Unreinforced, general purpose. Typical viscosity 5000-7000.

General Information
Features	General Purpose
Uses	General Purpose
Processing Method	Injection Molding
Multi-Point Data	Coefficient of Thermal Expansion vs. Temperature (ASTM E831) Elastic Modulus vs Temperature (ASTM D4065) Flexural DMA (ASTM D4065) Pressure-Volume-Temperature (PVT - Zoller Method) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Creep (ASTM D2990) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530) Viscosity vs. Shear Rate (ASTM D3835)

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.31	g/cm³	ASTM D792
Specific Volume	0.770	cm³/g	ASTM D792
Molding Shrinkage			Internal Method
Flow ¹	0.90 to 1.6	%
Flow ²	1.5 to 2.3	%
Across Flow ³	1.0 to 1.7	%
Across Flow ⁴	1.6 to 2.4	%
Water Absorption (24 hr)	0.080	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	117		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ⁵			ASTM D638
Yield	51.7	MPa
Break	51.7	MPa
Tensile Elongation ⁶(Break)	300	%	ASTM D638
Flexural Modulus ⁷(50.0 mm Span)	2340	MPa	ASTM D790
Flexural Strength ⁸			ASTM D790
Yield, 50.0 mm Span	82.7	MPa
Break, 50.0 mm Span	82.7	MPa

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C)	53	J/m	ASTM D256
Unnotched Izod Impact (23°C)	1600	J/m	ASTM D4812
Gardner Impact			ASTM D3029
23°C	40.7	J
23°C ⁹	40.7	J

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, Unannealed, 6.40 mm	154	°C
1.8 MPa, Unannealed, 6.40 mm	54.4	°C
CLTE - Flow			ASTM E831
-40 to 40°C	8.1E-5	cm/cm/°C
60 to 138°C	1.4E-4	cm/cm/°C
RTI Elec	120	°C	UL 746
RTI Imp	120	°C	UL 746
RTI Str	140	°C	UL 746

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	> 4.0E+16	ohms·cm	ASTM D257
Dielectric Strength			ASTM D149
1.60 mm, in Air	23	kV/mm
1.60 mm, in Oil	23	kV/mm
3.20 mm, in Air	16	kV/mm
3.20 mm, in Oil	16	kV/mm
Dielectric Constant			ASTM D150
100 Hz	3.30
1 MHz	3.10
Dissipation Factor			ASTM D150
100 Hz	2.0E-3
1 MHz	0.020
Arc Resistance ¹⁰	PLC 5		ASTM D495
Comparative Tracking Index (CTI)	PLC 0		UL 746
High Voltage Arc Tracking Rate (HVTR)	PLC 1		UL 746

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.47 mm)	HB		UL 94

Fill Analysis	Nominal Value	Unit	Test Method
Melt Viscosity	600	Pa·s	Internal Method

Injection	Nominal Value	Unit
Drying Temperature	121	°C
Drying Time	3.0 to 4.0	hr
Drying Time, Maximum	12	hr
Suggested Max Moisture	0.020	%
Suggested Shot Size	40 to 80	%
Rear Temperature	232 to 249	°C
Middle Temperature	238 to 254	°C
Front Temperature	243 to 260	°C
Nozzle Temperature	238 to 254	°C
Processing (Melt) Temp	243 to 260	°C
Mold Temperature	48.9 to 76.7	°C
Back Pressure	0.345 to 0.689	MPa
Screw Speed	50 to 100	rpm
Vent Depth	0.013 to 0.025	mm

Note Message
1 .	0.75 to 2.3 mm
2 .	2.3 to 4.6 mm
3 .	0.75 to 2.3 mm
4 .	2.3 to 4.6 mm
5 .	Type I, 50 mm/min
6 .	Type I, 50 mm/min
7 .	1.3 mm/min
8 .	1.3 mm/min
9 .	Modified
10 .	Tungsten Electrode

Resin Grade	Manufacturer	Category	Trademark
RTP ESD C 205 UV	RTP Company	Nylon 66	RTP
TOTAL Polystyrene Impact 8265	TOTAL Refining & Chemicals	PS (HIPS)	TOTAL Polystyrene
AMTOPP WT30	Inteplast Group	PP, Unspecified	AMTOPP
Clyrell EC348P	LyondellBasell Industries	PP, Unspecified	Clyrell
KumhoSunny PA/ABS HNA0370	Shanghai KumhoSunny Plastics Co., Ltd.	ABS+Nylon	KumhoSunny PA/ABS