GAPEX® APP40GR17HB-NA
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ferro Corporation |
| Trademark: | GAPEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MUBl7Y_GAPEX-APP40GR17HB-NA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GAPEX®APP40GR17HB-NA is a polypropylene homopolymer (PP Homopoly) material, which contains 40% glass \minerals. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. GAPEX®The main features of the APP40GR17HB-NA are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 | % | ASTM D955 |
| Transverse flow | 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 63.4 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 3.0 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% secant : 23°C | 4850 | MPa | ASTM D790 |
| Tangent : 23°C | 5310 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 95.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact | 290 | J/m | ASTM D256 |
| Dart Drop Impact | 0.226 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 154 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 143 | °C | ASTM D648 |
| Additional Information |
|---|
| The value listed as Unnotched Izod Impact, ASTM D256, was tested in accordance with ASTM D4812.Filler Content, ASTM D2584: 40.0%Testing and measurements were performed at 73 +/-3°F and 50 +/-5% relative humidity unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 GB 30 DEL | RTP Company | Acetal (POM) Homopolymer | RTP |
| SEETEC LLDPE UL912A | Lotte Chemical Corporation | LLDPE | SEETEC LLDPE |
| Geon™ Vinyl Dry Blend E7857 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Dry Blend |
| Jiangsu Meilan XXMLF2-10 | Jiangsu Meilan Chemical Co., Ltd. | Fluorelastomer | Jiangsu Meilan |
| OmniLon™ PA6 IM20 | OMNI Plastics, LLC | Nylon 6 | OmniLon™ |