TAISOX 6330F
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | TAISOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MU3ZiZ_TAISOX-6330F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TAISOX 6330F is a low density polyethylene material,. This product is available in North America, Europe or Asia Pacific,. The main features of TAISOX 6330F are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.1 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 53 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 9.81 | MPa | ASTM D638 |
| Fracture | 14.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 600 | % | ASTM D638 |
| Flexural Modulus | 177 | MPa | ASTM D790 |
| Coefficient of Friction (Blown Film) | 0.50 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Film Thickness - Recommended / Available | 1-3.1 mil (25-80 µ) | ||
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 30 µm, blown film | 196 | MPa | ASTM D882 |
| 1% secant, TD : 30 µm, blown film | 226 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 30 µm, blown film | 9.81 | MPa | ASTM D882 |
| TD : Yield, 30 µm, blown film | 10.8 | MPa | ASTM D882 |
| MD : Broken, 30 µm, blown film | 22.6 | MPa | ASTM D882 |
| TD : Broken, 30 µm, blown film | 17.7 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 30 µm, blown film | 280 | % | ASTM D882 |
| TD : Broken, 30 µm, blown film | 580 | % | ASTM D882 |
| Dart Drop Impact (30 µm, Blown Film) | 100 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 30 µm, blown film | 210 | g | ASTM D1922 |
| TD : 30 µm, blown film | 150 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 96.0 | °C | ASTM D1525 |
| Melting Temperature | 113 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 30.0 µm, Blown Film) | 95 | ASTM D2457 | |
| Haze (30.0 µm, Blown Film) | 6.5 | % | ASTM D1003 |
| Additional Information |
|---|
| Film extrusion preparation parameters: Screw: 60 mm L/D: 30 Blow up ratio: 2.5 Temperature160 to 200°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Yuyao PBT 3055G30 | Yuyao Tenglong Plastics Co., Ltd. | PBT | Yuyao PBT |
| NORYL GTX™ GTX8120P resin | SABIC Innovative Plastics Europe | PPE+PS+Nylon | NORYL GTX™ |
| APEX® 90-A482R-70-NT | Teknor Apex Company | PVC, Flexible | APEX® |
| EPAMOULD 293A33 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |
| Sylvin 4200-75UV Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |