Versaflex™ 9555-9
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Versaflex™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MS8kKX_Versaflex-9555-9.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Versaflex™9555-9 has strong fluidity, good surface aesthetics, and is suitable for various applications.
|
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.988 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 4.1 | g/10 min | ASTM D1238 |
| 200°C/5.0 kg | 27 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.90 - 1.7 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 53 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ASTM D412 | ||
| 100% strain, 23°C 2 | 1.45 | MPa | ASTM D412 |
| 300% strain, 23°C 3 | 2.31 | MPa | ASTM D412 |
| Tensile Strength (Break, 23°C) | 3.90 | MPa | ASTM D412 |
| Tensile Elongation (Break, 23°C) | 580 | % | ASTM D412 |
| Compression Set (23°C, 22 hr) | 20 | % | ASTM D395B |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Viscosity | ASTM D3835 | ||
| 200°C, 1340 sec^-1 | 35.0 | Pa·s | ASTM D3835 |
| 200°C, 11200 sec^-1 | 7.20 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 149 - 188 | °C | |
| Middle Temperature | 160 - 199 | °C | |
| Front Temperature | 171 - 210 | °C | |
| Nozzle Temperature | 171 - 210 | °C | |
| Mold Temperature | 15.6 - 26.7 | °C | |
| Back Pressure | 0.00 - 0.689 | MPa | |
| Screw Speed | 50 - 100 | rpm |
| Injection instructions |
|---|
| 在使用此产品之前或之后，均须用熔体流动速率较低 (0.5 - 2.5 MFR) 的聚乙烯 (PE) 或聚丙烯 (PP) 彻底进行置换。Versaflex™ 9555-9 可利用高达 20% 的回收料同时其性能所受影响却极小，但该回收料必须是未受到污染的。为了最大限度地减小模塑期间其性能所受的影响，熔体温度应维持得尽可能低。回收料的有效性应由用户最终确定。Versaflex™ 9555-9 具有良好的熔体稳定性。如果机器闲置十五 (15) 分钟或以上，则应将机筒排空。不需要干燥注射速度：1 - 5 英寸/秒第一阶段 - 提升压力：300 - 700 psi第二阶段 - 保持压力：30% 的升压保持时间（厚部件）：4 - 10 秒保持时间（薄部件）：1 - 3 秒 |
| Note Message | |
|---|---|
| 1 . | 2 hours |
| 2 . | Mouth die c |
| 3 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Varcum 29116 | Durez Corporation | Phenolic | Varcum |
| Acculam™ Phenolkraft Paper XX/XXX | Accurate Plastics, Inc. | Phenolic | Acculam™ |
| CYCOLOY™ C2800 resin | SABIC Innovative Plastics | PC+ABS | CYCOLOY™ |
| Delrin® Stock Shapes AF Blend | Ensinger Inc. | Acetal (POM) Homopolymer | Delrin® Stock Shapes |
| Karina CRYSTAL PVC COM. (SP32811) -E 72/206-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Flexible | Karina |