NORYL™ FNH2160 resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MRLSy2_NORYL-FNH2160-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Non brominated non chlorinated flame retarded NORYL resin for structural foam applications. 80C HDT. All values at 20% weight reduction. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- 1 | 0.878 | g/cm³ | ASTM D792 |
| -- | 1.12 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 36.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (6.40 mm) | 0.50 - 0.80 | % | Internal method |
| Water Absorption (24 hr) | 0.070 | % | ASTM D570 |
| Foam - Physical 2 | 20 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Foam - Mechanical 3 | 20 | % | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Foam - Impact 4 | 20 | % | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Foam - Thermal 5 | 20 | % | Internal method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Foam - Flame Class Minimum Density | 850 | kg/m³ | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 6.35mm | 36.0 | MPa | ASTM D638 |
| Fracture, 6.35mm | 34.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 6.35 mm) | 12 | % | ASTM D638 |
| Flexural Modulus (6.40 mm) | 2250 | MPa | ASTM D790 |
| Flexural Strength (Yield, 6.40 mm) | 70.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C, 6.40 mm) | 360 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 29.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 93.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 82.0 | °C | ASTM D648 |
| RTI Elec | 65.0 | °C | UL 746 |
| RTI Imp | 65.0 | °C | UL 746 |
| RTI | 65.0 | °C | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 3.00 mm | V-1 | UL 94 | |
| 6.00 mm | V-0 | UL 94 | |
| 3.90 mm | 5VA | UL 94 |
| Additional Information |
|---|
| Structural Foam Molding - Blowing Agent, Physical System: Nitrogen GasStructural Foam Molding - Concentration Range (Blowing Agent): 1 - 3 %Structural Foam Molding - Drying Temperature (Resin): 71 - 82 °CStructural Foam Molding - Drying Time (Resin): 2 - 4 hrsStructural Foam Molding - Drying Time (Resin, Cumulative): 8 hrsStructural Foam Molding - Front Temperature: 271 - 304 °CStructural Foam Molding - Melt Temperature: 271 - 310 °CStructural Foam Molding - Middle Temperature: 271 - 304 °CStructural Foam Molding - Mold Temperature: 27 - 54 °CStructural Foam Molding - Nozzle Temperature: 271 - 304 °CStructural Foam Molding - Rear Temperature: 232 - 260 °CStructural Foam Molding - Recommended Concentration (Blowing Agent): 2 % |
| Note Message | |
|---|---|
| 1 . | Foam molded |
| 2 . | 6.4 mm wt reduction |
| 3 . | 6.4 mm wt reduction |
| 4 . | 6.4 mm wt reduction |
| 5 . | 6.4 mm wt reduction |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Chemlon® 509 | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| COSMOTHENE® EVA D5010 | TPC, The Polyolefin Company (Singapore) Pte Ltd | EVA | COSMOTHENE® EVA |
| Durethan® BKV 30 H2.0 EF 901510 | LANXESS GmbH | Nylon 6 | Durethan® |
| Elastron® D D100.A72.B | Elastron USA, Inc. | SBS | Elastron® D |
| ALTECH® PC ECO 1000/141 | ALBIS PLASTIC GmbH | PC | ALTECH® PC |