KRATON® D1114 P
| Category: | SIS , Styrene Isoprene Styrene Block Copolymer |
| Manufacturer: | Kraton Polymers LLC |
| Trademark: | KRATON® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MRGYLK_KRATON-D1114-P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Kraton D1114 P is a clear, linear triblock copolymer based on styrene and isoprene with a polystyrene content of 19%. It is suppliedfrom North America in the physical form identified below.
Kraton D1114 P is used as an ingredient in formulating adhesives, sealants and coatings. It may also find use as a modifier of bitumen or thermoplastics and in compound formulations. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.920 | g/cm³ | ASTM D4025 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 7.0 to 13 | g/10 min | ASTM D1238 |
| Antioxidant Additive 1 | 0.080 to 0.30 | % | Internal Method |
| Ash Content | |||
| PSM 2 | 2.5 to 5.0 | % | ISO 247 |
| Talc | 0.2 to 0.4 | wt% | Internal Method |
| Polystyrene Content | 17 to 21 | % | Internal Method |
| Solution Viscosity - Toluene, 25%w (25°C) | 600 to 1000 | mPa·s | Internal Method |
| Total Extractables | < 1.0 | % | Internal Method |
| Volatile Matter | < 0.50 | % | Internal Method |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Diblock Content | < 1.00 | ||
| Styrene/Rubber ratio | 19/81 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (300% Strain) | 1.86 | MPa | ASTM D412 |
| Tensile Strength (Yield) | 31.7 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 1300 | % | ASTM D412 |
| Note Message | |
|---|---|
| 1 . | Primary antioxidant is a non-staining, phenolic antioxidant. The antioxidant package also contains a non-TNPP secondary antioxidant at a target level of 0.2% wt. |
| 2 . | The final dusting level is a combination of the talc from the original D1114 PT and silica added during the milling process. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| StarXTRUDE XTR-55-1000 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | StarXTRUDE |
| Arnitel® EM400 | DSM Engineering Plastics | TPC-ET | Arnitel® |
| ASI POLYPROPYLENE PP 3369-01 | A. Schulman Inc. | PP Homopolymer | ASI POLYPROPYLENE |
| Geon™ Vinyl Flexible A8001 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| LNP™ LUBRICOMP™ RFL34 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |